Synthesis of a Regioregular Series of Poly(aryl ether carbonates) and Their Glass Transition Temperatures.

Autor: Alomar MS; Department of Chemical Engineering Technology, Jazan University, Jazan 45142, Saudi Arabia., Boyles DA; Jack R. Gaines Emeritus Professor of Chemistry, Department of Chemistry and Applied Biological Sciences, South Dakota School of Mines and Technology, Rapid City, South Dakota 57701, United States.
Jazyk: angličtina
Zdroj: ACS omega [ACS Omega] 2019 Dec 19; Vol. 4 (27), pp. 22363-22372. Date of Electronic Publication: 2019 Dec 19 (Print Publication: 2019).
DOI: 10.1021/acsomega.9b02648
Abstrakt: Bisphenol A polycarbonate (BPA-PC) is a remarkable high-performance engineering polymer, although it is susceptible to photo-Fries and hydrolytic degradation. New poly(aryl ether carbonates) were synthesized to address these limitations by replacing the chain backbone carbonate ester functionality with aryl ether functionality. The monomers for these new polymers were synthesized by a variation of the Ullmann condensation accelerated by 2,2,6,6-tetramethylheptane-3,5-dione and promoted by Cs 2 CO 3 and 1-methyl-2-pyrrolidinone under mild conditions. Four such bisphenol A-based diarylether monomers containing different mass ratios of carbonate ester groups were prepared and polymerized with phosgene gas to give novel poly(aryl ether carbonates). Polymers were named as di- o -BPA-PC 9' , tri- o -BPA-PC 11' , tetra- o -BPA-PC 13' , and penta- o -BPA-PC 15' where di-, tri-, tetra-, and penta- reflect the number of diphenylisopropylidene units in each of the respective polymers. The molecular weights of the resulting four poly(aryl ether carbonates) were measured by gel permeation chromatography. Differential scanning calorimetry was used to measure glass transition temperature ( T g ). The polymers exhibited weight-average molecular weights up to 4.09 × 10 5 g/mol and T g in the range of 136 to 149 °C with no melting temperature peak, indicative of their amorphous character. The new polymers formed transparent and flexible films by solution casting from chloroform solution.
Competing Interests: The authors declare no competing financial interest.
(Copyright © 2019 American Chemical Society.)
Databáze: MEDLINE
Externí odkaz: