Riley BJ; Pacific Northwest National Laboratory , Richland, Washington 99354, United States., Kroll JO; Pacific Northwest National Laboratory , Richland, Washington 99354, United States., Peterson JA; Pacific Northwest National Laboratory , Richland, Washington 99354, United States., Matyáš J; Pacific Northwest National Laboratory , Richland, Washington 99354, United States., Olszta MJ; Pacific Northwest National Laboratory , Richland, Washington 99354, United States., Li X; Pacific Northwest National Laboratory , Richland, Washington 99354, United States., Vienna JD; Pacific Northwest National Laboratory , Richland, Washington 99354, United States. |
| Abstrakt: |
In this paper, aluminosilicate aerogels were used as scaffolds for silver nanoparticles to capture I 2 (g). The starting materials for these scaffolds included Na-Al-Si-O and Al-Si-O aerogels, both synthesized from metal alkoxides. The Ag 0 particles were added by soaking the aerogels in aqueous AgNO 3 solutions followed by drying and Ag + reduction under H 2 /Ar to form Ag 0 crystallites within the aerogel matrix. In some cases, aerogels were thiolated with 3-(mercaptopropyl)trimethoxysilane as an alternative method for binding Ag + . During the Ag + -impregnation steps, for the Na-Al-Si-O aerogels, Na was replaced with Ag, and for the Al-Si-O aerogels, Si was replaced with Ag. The Ag-loading of thiolated versus nonthiolated Na-Al-Si-O aerogels was comparable at ∼35 atomic %, whereas the Ag-loading in unthiolated Al-Si-O aerogels was significantly lower at ∼7 atomic % after identical treatment. Iodine loadings in both thiolated and unthiolated Ag 0 -functionalized Na-Al-Si-O aerogels were >0.5 m I m s -1 (denoting the mass of iodine captured per starting mass of the sorbent) showing almost complete utilization of the Ag through chemisorption to form AgI. Iodine loading in the thiolated and Ag 0 -functionalized Al-Si-O aerogel was 0.31 m I m s -1 . The control of Ag uptake over solution residence time and [Ag] demonstrates the ability to customize the Ag-loading in the base sorbent to regulate the loading capacity of iodine. |