Autor: |
Lee JH; Center for Intelligent Nano-Bio Materials (CINBM), Department of Bioinspired Science, Ewha Womans University, Seoul, Korea., Choi G, Oh YJ, Park JW, Choy YB, Park MC, Yoon YJ, Lee HJ, Chang HC, Choy JH |
Jazyk: |
angličtina |
Zdroj: |
International journal of nanomedicine [Int J Nanomedicine] 2012; Vol. 7, pp. 1635-49. Date of Electronic Publication: 2012 Mar 26. |
DOI: |
10.2147/IJN.S28264 |
Abstrakt: |
A nanohybrid was prepared with an inorganic clay material, montmorillonite (MMT), for taste masking of sildenafil (SDN). To further improve the taste-masking efficiency and enhance the drug-release rate, we coated the nanohybrid of SDN-MMT with a basic polymer, polyvinylacetal diethylaminoacetate (AEA). Powder X-ray diffraction and Fourier transform infrared experiments showed that SDN was successfully intercalated into the interlayer space of MMT. The AEA-coated SDN-MMT nanohybrid showed drug release was much suppressed at neutral pH (release rate, 4.70 ± 0.53%), suggesting a potential for drug taste masking at the buccal cavity. We also performed in vitro drug release experiments in a simulated gastric fluid (pH = 1.2) and compared the drug-release profiles of AEA-coated SDN-MMT and Viagra(®), an approved dosage form of SDN. As a result, about 90% of SDN was released from the AEA-coated SDN-MMT during the first 2 hours while almost 100% of drug was released from Viagra(®). However, an in vivo experiment showed that the AEA-coated SDN-MMT exhibited higher drug exposure than Viagra(®). For the AEA-coated SDN-MMT, the area under the plasma concentration- time curve from 0 hours to infinity (AUC(0-∞)) and maximum concentration (C(max)) were 78.8 ± 2.32 μg · hour/mL and 12.4 ± 0.673 μg/mL, respectively, both of which were larger than those obtained with Viagra(®) (AUC(0-∞) = 69.2 ± 3.19 μg · hour/mL; C(max) = 10.5 ± 0.641 μg/mL). Therefore, we concluded that the MMT-based nanohybrid is a promising delivery system for taste masking of SDN with possibly improved drug exposure. |
Databáze: |
MEDLINE |
Externí odkaz: |
|