Autor: |
Konstantin N. Gorbachenya, Elena A. Volkova, Victor V. Maltsev, Victor E. Kisel, Diana D. Mitina, Elizaveta V. Koporulina, Nikolai N. Kuzmin, Ekaterina I. Marchenko, Vladimir L. Kosorukov |
Jazyk: |
angličtina |
Rok vydání: |
2024 |
Předmět: |
|
Zdroj: |
Inorganics, Vol 12, Iss 9, p 240 (2024) |
Druh dokumentu: |
article |
ISSN: |
2304-6740 |
DOI: |
10.3390/inorganics12090240 |
Popis: |
A transparent Er3+,Yb3+:GdMgB5O10 single crystal with dimensions up to 24 × 15 × 12 mm was grown successfully by the high-temperature solution growth on dipped seeds technique from K2Mo3O10-based solvent. The grown crystal was characterized using PXRD, DSC and ATR techniques. Differential scanning calorimetry measurements and SEM analysis of the heat-treated solids revealed Er,Yb:GdMgB5O10 to be an incongruent melting compound with an onset point of 1087 °C. The absorption edge of the Er,Yb:GMBO sample is located in the region of 245 nm, which approximates a value of 4.8 eV. Absorption and emission spectra, and luminescence kinetics, were studied. The energy transfer efficiency from ytterbium to erbium ions was determined. The laser operation in continuous-wave mode was realized and output characteristics were measured. The maximal output power of 0.15 W with a slope efficiency of 11% was obtained at 1568 nm. |
Databáze: |
Directory of Open Access Journals |
Externí odkaz: |
|
Nepřihlášeným uživatelům se plný text nezobrazuje |
K zobrazení výsledku je třeba se přihlásit.
|