Autor: |
Yu CAO, Peng CHEN, Jiangong YANG, Deqiang WANG, Yong BAI |
Jazyk: |
English<br />Chinese |
Rok vydání: |
2024 |
Předmět: |
|
Zdroj: |
Zhongguo Jianchuan Yanjiu, Vol 19, Iss 4, Pp 186-192 (2024) |
Druh dokumentu: |
article |
ISSN: |
1673-3185 |
DOI: |
10.19693/j.issn.1673-3185.03616 |
Popis: |
ObjectiveThis study aims to explore the structural strength deterioration mechanism of pipelines with corrosion defects in hydrogen-blended environments.MethodsBased on the experimental data, an analysis is made of the load bearing performance of X52 steel under different levels of hydrogen blending , and the structural strength failure mechanism of an X52 hydrogen-blended natural gas pipeline under different corrosion defects is described using the nonlinear finite element method. ResultsWhen the hydrogen blend level increases to 50.0%, under a combined load, the pipeline reaches minimum displacement failure at 2.58 mm, and the structural toughness deteriorates to a greater degree; at a hydrogen blend level of 25.0%, the defect depth is greater and the degree of structural failure more serious; comparing square and circular defects, the maximum stress of the square defects is higher than that of the circular defects. ConclusionsThe material property-based defective pipeline model can realize the assessment of the structural bearing capacity deterioration of natural gas pipelines under different hydrogen-blending conditions, providing engineering suggestions for the design and health monitoring of new energy pipelines. |
Databáze: |
Directory of Open Access Journals |
Externí odkaz: |
|