| Popis: |
The paper aims at addressing the effect of the bonding time on the metallurgical and mechanical properties of a transient-liquid-phase (TLP) bonded IN718 nickel-based superalloy using an Ni-15.2Cr-4B (%) amorphous filler alloy. The results showed that after a partial isothermal solidification, the residual liquid in the joint centerline transformed, during the cooling, to non-equilibrium eutectic-type microconstituents composed of Ni-rich boride, Cr-rich boride and eutectic g-solid solution phase. The complete isothermal solidification which resulted in a formation of an intermetallic-free joint centerline occurred after a holding period 40 min at the bonding temperature of 1100 °C. An increase in the bonding time improved the joint shear strength due to a decrease in the width of the eutectic-type microconstituents in the joint centerline. Članek obravnava vpliv časa spajanja na metalurške in mehanske lastnosti nikljeve superzlitine IN718, spojene s prehodno tekočo fazo (TLP) in z uporabo Ni-15,2Cr-4B (%) amorfnega polnila. Rezultati kažejo, da se po delnem izotermnem strjevanju preostala talina v sredini spoja pretvori pri ohlajanju v neravnotežno sestavino evtektičnega tipa, ki jo sestavljajo z Ni bogati boridi, s Cr bogati boridi in evtektična g- trdna raztopina. Popolno izotermno strjevanje je bilo doseženo po 40 min zadrževanja pri 1100 °C, pri čemer je nastala sredica spoja brez intermetalnih zlitin. Podaljšanje časa spajanja je izboljšalo strižno trdnost spoja zaradi zmanjšanja širine sestavine evtektičnega tipa v sredini spoja. |