Спектроскопія домішкових станів у сплавах Cu−Mn
| Autor: | Stashchuk, V.S., Bondar, V.M., Polianska, O.P., Filipov, Ya.V. |
|---|---|
| Jazyk: | ukrajinština |
| Rok vydání: | 2022 |
| Zdroj: | Ukrainian Journal of Physics; Vol. 56 No. 4 (2011); 327 Український фізичний журнал; Том 56 № 4 (2011); 327 |
| ISSN: | 2071-0194 2071-0186 |
| DOI: | 10.15407/ujpe56.4 |
| Popis: | The indices of refraction n and absorption χ of disordered Cu–Mn alloys with manganese concentrations of 2, 5, 10, 17.5, 25,37.5, and 50% are measured in the spectral range 0.23–2.8 μm (0.44–5.39 eV) at room temperature using the ellipsometric technique. Based on these data, the optical conductivity σrelated to interband transitions is calculated. The collision frequency γ and the concentration of conduction electrons N are determined in the intraband absorption region. It is established that the addition of manganese results in the formation of a new impurity band in the copper electron spectrum which is located by 2.2 eV lower than the Fermi level and is split into two energy subbands due to the exchange interaction. Еліпсометричним методом при кімнатній температурі виміряно показники заломлення n та поглинання χ невпорядкованих сплавів Cu–Mn з концентраціями 2; 5; 10; 17,5; 25; 37,5 та 50% марганцю в широкому спектральному діапазоні 0,23–2,8 мкм (0,44–5,39 еВ). На основі цих даних розраховано оптичну провідність σ, яка пов'язана з міжзонними переходами. В області внутрішньозонного поглинання визначено частоту зіткнень γ та концентраціюелектронів провідності N. Встановлено, що в електронному спектрі міді при додаванні марганцю формується нова домішкова зона, розташована на відстані 2,2 еВ нижче від рівня Фермі, і яка розщеплюється внаслідок обмінної взаємодії на дві енергетичні підзони. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|