Development of design methodology of technological process of ball-rod hardening with account for formation of compressive residual stresses
| Autor: | S. A. Morozov, M. A. Tamarkin, E. E. Tishchenko, S. A. Novokreshchenov |
|---|---|
| Rok vydání: | 2020 |
| Předmět: |
Materials science
ball-rod hardening Sharpening Fatigue limit Machining hardened layer depth Residual stress residual stresses Management of Technology and Innovation surface roughness TA401-492 Surface roughness Hardening (metallurgy) Surface layer deformation ratio Composite material Materials of engineering and construction. Mechanics of materials Interference fit |
| Zdroj: | Advanced Engineering Research, Vol 20, Iss 2, Pp 143-149 (2020) |
| ISSN: | 1992-6006 1992-5980 |
| Popis: | Introduction . The study results on the multicontact shock-vibrating machining using a ball-rod hardener are presented. Methods of surface plastic deformation processing, their advantages are described. The tool circuit diagram is given. Features, technological advantages, and the application area of the ball-rod hardening are specified. Materials and Methods . When conducting theoretical studies on the processing, factors, which affect the quality of the surface layer of the machined parts, were established. Dependences are given for calculating the surface roughness, the hardened layer depth, and the deformation ratio under ball-rod hardening. While studying the generation of residual stresses, the dependence for calculating the residual stresses generated in the surface layer of the machined part was specified. Results . The experimental findings of the processing requisite for verification of the adequacy of the theoretical models, as well as the routine of the experiments, are presented. A table and graphs clearly confirming good convergence of the theoretical and experimental data are given (the difference does not exceed 20%). Residual stresses in the surface layer are compressive which enables to predict high performance properties of the machined parts. The value of residual stresses on the workpiece surface is in the range of 130÷200 MPa. The depth of compressive residual stresses is in the range of 0.9-1 mm. The fatigue characteristic variation, the ultimate stresses of the cycle in depth, which affects the endurance limit, is calculated. It has been established that the processing of workpieces by a ball-rod hardener provides increasing the ultimate cycle stress under repeated loading by 27-35%. Discussions and Conclusions . The design methodology of technological process of ball-rod hardening can be used under the development of production at the machine-building enterprises. In accordance with the recommendations, the limits of the required quality parameters of the workpiece surface layer are set; the parameters of the ball-rod hardener, the interference fit and the radius of rod sharpening are selected. Quality parameters of the surface layer are calculated. Correction of the selected modes and re-calculation of the parameters of the machined surface are carried out until all the specified characteristics are located within the required limits. |