Enhancement Magneto-optic Properties of Radio-Frequency-Magnetron-sputtered Bi-containing Ferrite Garnet-Type Thin-films using Oxygen plasma treatment and metal-oxide protective layers
| Autor: | D. E. Balabanov, Kamal Alameh, Mikhail Vasiliev, Mohammad Nur E Alam, V. A. Kotov, Vladimir I. Burkov |
|---|---|
| Rok vydání: | 2020 |
| Předmět: |
Materials science
business.industry Oxide Polarization (waves) Metal chemistry.chemical_compound symbols.namesake surfaces _coatings_films chemistry visual_art Faraday effect symbols visual_art.visual_art_medium Optoelectronics Figure of merit Ferrite (magnet) Radio frequency magnetron Thin film business |
| DOI: | 10.20944/preprints202010.0014.v1 |
| Popis: | Magneto-optic (MO) imaging and sensing are at present the most developed practical applications of thin-film MO garnet materials. However, future component and system-level sensors and imagers technology improvements are still necessary in order to improve sensitivity for a range of established and also the forward-looking applications. These improvements are expected to originate from new material system development. We propose a set of technological modifications for the RF-magnetron sputtering deposition and crystallization annealing of magneto-optic bismuth-substituted iron-garnet films and investigate the improved material properties. Results show that standard crystallization annealing for the as-deposited ultrathin (sputtered 10 nm thick, amorphous phase) films resulted in more than a factor of two loss in the magneto-optical activity of the films in visible spectral region, compared to the liquid-phase grown epitaxial films. Results also show that an additional 10 nm-thick metal-oxide (Bi2O3) protective layer above the amorphous film results in ~2.7 times increase in the magneto-optical quality of crystallized iron-garnet films. On the other hand, the effects of post-deposition oxygen (O2) plasma treatment on the magneto-optical (MO) properties of Bismuth substituted iron garnet thin films material is investigated. Results show that, in the visible part of the electromagnetic spectrum (at 532 nm), the O2 treated (up to 3 minutes) garnet films retain higher specific Faraday rotation and figure of merit than those of non-treated garnet films. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|