Effects of Bismuth on the Microstructure, Properties, and Interfacial Reaction Layers of Sn-9Zn-xBi Solders
| Autor: | Cun Ji Pu, Jian Hong Yi, Jiao Jiao Yang, Jia Tao Zhang, Yan Zhi Peng, Guang Ji Zhou, Ju Bo Peng, Li Caiju |
|---|---|
| Rok vydání: | 2021 |
| Předmět: |
oxidation resistance
lcsh:TN1-997 Materials science intermetallic microstructure Alloy chemistry.chemical_element 02 engineering and technology Liquidus Solidus engineering.material 01 natural sciences Bismuth Phase (matter) 0103 physical sciences General Materials Science Composite material lcsh:Mining engineering. Metallurgy lead-free 010302 applied physics Metals and Alloys 021001 nanoscience & nanotechnology Microstructure chemistry Soldering solder alloy engineering 0210 nano-technology Solid solution |
| Zdroj: | Metals, Vol 11, Iss 538, p 538 (2021) Metals Volume 11 Issue 4 |
| ISSN: | 2075-4701 |
| Popis: | In electronic packaging, Sn-Zn lead-free solder has great application prospects. Sn-9Zn-xBi alloys were obtained by smelting. This paper details a systematic study of the effect of Bi on the microstructure, melting behavior, wettability, mechanical behavior, antioxidant properties, and electrical conductivity of Sn-9Zn-xBi alloy, as well as the interfacial reaction in Sn-9Zn-xBi/Cu joints. The coarse Zn-rich phase became larger with an increase in the addition of Bi, which is harmful to the oxidation resistance of the solders. The melting temperature, solidus temperature, and liquidus temperature decreased with the increase in the addition of Bi, but the melting range increased. Adding a proper amount of Bi could substantially improve the spreading rate of Sn-9Zn, but reduce its oxidation resistance. Because of the solid solution effect of Bi element, the tensile strength of the Sn-9Zn solders could be enhanced, but the plastic and electrical conductivity was decreased. The IMC layer of the Sn-9Zn and Cu joints consisted of the ε-CuZn5 phase and the γ-Cu5Zn8 phase. With an increase in the Bi element, the thickness of the interfacial reaction layer was firstly increased. When the Bi element content exceeded 3 wt.%, the inhibitory effect of the aggregated Bi elements on the formation of IMC was greater than the positive effect of the longer reaction time, and the thickness of the IMC decreased. |