Accurate quantitative EDS-TEM analysis of precipitates and matrix in equilibrium (α+β) Zr–1Nb alloys with Ta addition
| Autor: | Gerardo Hector Rubiolo, Pedro Antonio Ferreirós, D.P. Quirós, E. Zelaya, P.R. Alonso |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2020 |
| Předmět: |
Ta addition
Materials science Alloy Analytical chemistry 02 engineering and technology ENERGY DISPERSIVE X-RAY SPECTROSCOPY (EDS) engineering.material 010402 general chemistry 01 natural sciences Matrix (chemical analysis) Phase (matter) Materials Chemistry TA ADDITION Transmission electron microscopy (TEM) Thin film Solubility Energy dispersive X-ray spectroscopy (EDS) TRANSMISSION ELECTRON MICROSCOPY (TEM) Mechanical Engineering Metals and Alloys 021001 nanoscience & nanotechnology Microstructure CLIFF-LORIMER FACTOR Zr-Nb alloys 0104 chemical sciences purl.org/becyt/ford/2 [https] Mechanics of Materials ZR-NB ALLOYS engineering Particle Cliff-lorimer factor 0210 nano-technology purl.org/becyt/ford/2.5 [https] Mass fraction |
| Zdroj: | CONICET Digital (CONICET) Consejo Nacional de Investigaciones Científicas y Técnicas instacron:CONICET Ferreirós, P A, Alonso, P R, Quirós, D P, Zelaya, E & Rubiolo, G H 2020, ' Accurate quantitative EDS-TEM analysis of precipitates and matrix in equilibrium (α+β) Zr–1Nb alloys with Ta addition ', Journal of Alloys and Compounds, vol. 847, 156372 . https://doi.org/10.1016/j.jallcom.2020.156372 |
| DOI: | 10.1016/j.jallcom.2020.156372 |
| Popis: | The (α+β) phase microstructure in Zr-1.05Nb, Zr-0.85Nb-0.20Ta and Zr-0.85Nb-0.40Ta (wt.%) alloys annealed at 570 °C for 3840 h after β-quenching were observed at different scales by optical, SEM and TEM microscopies. A quantitative study of phase chemical compositions was carried out by EDS-TEM with experimental Cliff-Lorimer factors. The α matrix was measured on thin films and the β particle on carbon extractive replicas. The Ta addition showed a continuous increase of (Nb + Ta) solubility in α-Zr and (Zr + Ta) solubility in the β-Nb phase. The increase of Ta in the nominal composition of the Zr-1(Nb, Ta) alloy causes the decrease of the mass fraction of β-Nb phase. Fil: Ferreirós, Pedro Antonio. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Unidad de Actividad de Materiales (CAC); Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Universidad Nacional de San Martín. Instituto Sabato; Argentina. Universidad Tecnológica Nacional. Facultad Regional Haedo; Argentina Fil: Alonso, P. R.. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Unidad de Actividad de Materiales (CAC); Argentina. Universidad Nacional de San Martín. Instituto Sabato; Argentina Fil: Quirós, D. P.. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Unidad de Actividad de Materiales (CAC); Argentina Fil: Zelaya, E.. Comisión Nacional de Energía Atómica. Centro Atómico Bariloche; Argentina Fil: Rubiolo, Gerardo Hector. Universidad Nacional de San Martín. Instituto Sabato; Argentina. Consejo Nacional de Investigaciones Científicas y Técnicas; Argentina. Comisión Nacional de Energía Atómica. Gerencia del Área de Energía Nuclear. Unidad de Actividad de Materiales (CAC); Argentina |