Concentrated sunlight for accelerated stability testing of organic photovoltaic materials: towards decoupling light intensity and temperature
| Autor: | Yulia Galagan, Leila Zeiri, Eugene A. Katz, Iris Visoly-Fisher, Maurizio Sansotera, Asaf Mescheloff, M. Gabay, A.E. Goryachev, Avi Braun, Céline Bounioux |
|---|---|
| Rok vydání: | 2015 |
| Předmět: |
P3HT:PCBM
Sunlight Condensed Matter - Materials Science Materials science Temperature control integumentary system Organic solar cell Renewable Energy Sustainability and the Environment business.industry Photovoltaic system Materials Science (cond-mat.mtrl-sci) FOS: Physical sciences Humidity Photon energy Suns in alchemy Surfaces Coatings and Films Electronic Optical and Magnetic Materials Degradation Light intensity Organic photovoltaics Concentrated sunlight Stability Optoelectronics business |
| Zdroj: | Solar Energy Materials and Solar Cells. 134:99-107 |
| ISSN: | 0927-0248 |
| Popis: | We have demonstrated accelerated degradation studies of organic photovoltaic materials using concentrated sunlight, where the atmosphere, temperature and illumination intensity were independently controlled. Testing various schemes for controlling the sample temperature under concentrated sunlight showed that heating of P3HT:PCBM was caused by photons at the absorbed wavelength range and dissipation of excess photon energy, and not necessarily by IR photon absorption. Sunlight chopping was found to be an effective method for independent temperature control under illumination by concentrated sunlight. The first accelerated degradation tests using sunlight concentration applied to P3HT:PCBM blends were reported. P3HT:PCBM blends exposed to concentrated sunlight in the presence of traces of oxygen/ humidity showed degradation induced by photo-oxidation of the P3HT backbone within the P3HT:PCBM blend, which is significantly thermally accelerated, in agreement with previous observations. However, this could be demonstrated in a time scale of minutes and hours, that is, significantly accelerated. Exposure of well encapsulated P3HT:PCBM films to concentrated sunlight demonstrated stability up to 3,600 sun⁎hours, corresponding to about 1.6 years of operating time. This result was obtained at 300 suns exposure after merely 12 h, demonstrating the advantage of using concentrated sunlight for accelerated stability tests. These tests can therefore combine extremely high acceleration factors with profound understanding of the effect of various, independently controlled factors on the degradation mechanisms. |