The Extrusion and SPS of Zirconium–Copper Powders and Studies of Selected Mechanical Properties
| Autor: | Marcin Podsiadło, Tomasz Skrzekut, Adam Zwoliński, Piotr Noga, Lucyna Jaworska, Grzegorz Boczkal, P. Pałka |
|---|---|
| Rok vydání: | 2021 |
| Předmět: |
Technology
Zr-Cu mixtures Materials science Intermetallic Spark plasma sintering Sintering SPS Fractography mechanical properties Article Brittleness Ultimate tensile strength General Materials Science Composite material Microscopy QC120-168.85 QH201-278.5 Engineering (General). Civil engineering (General) Microstructure TK1-9971 zirconium powders Descriptive and experimental mechanics microstructures SEM Extrusion Electrical engineering. Electronics. Nuclear engineering TA1-2040 |
| Zdroj: | Materials Materials, Vol 14, Iss 3560, p 3560 (2021) Volume 14 Issue 13 |
| ISSN: | 1996-1944 |
| Popis: | Zr-2.5Cu and Zr-10Cu powder mixtures were consolidated in the extrusion process and using the spark plasma sintering technique. In these studies, material tests were carried out in the fields of phase composition, microstructure, hardness and tensile strength for Zr-Cu materials at room temperature (RT) and 400 °C. Fractography analysis of materials at room temperature and 400 °C was carried out. The research took into account the anisotropy of the materials obtained in the extrusion process. For the nonequilibrium SPS process, ZrCu2 and Cu10Zr7 intermetallic compounds formed in the material at sintering temperature. Extruded materials were composed mainly of α-Zr and ZrCu2. The presence of intermetallic compounds affected the reduction in the strength properties of the tested materials. The highest strength value of 205 MPa was obtained for the extruded Zr-2.5Cu, for which the samples were cut in the direction of extrusion. For materials with 10 wt.% copper, more participation of the intermetallic phase was formed, which lowered the mechanical properties of the obtained materials. In addition to brittle intermetallic phases, the materials were characterized by residual porosity, which also reduced the strength properties. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
| Nepřihlášeným uživatelům se plný text nezobrazuje | K zobrazení výsledku je třeba se přihlásit. |