Silica-Kaolin Mix Effect on Evaporative Pattern Castings Surface Roughness
| Autor: | M. S. Abolarin, RH Khan, Babatunde Victor Omidiji |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2016 |
| Předmět: |
Binder
Materials science Pattern 05 social sciences Metallurgy Metals and Alloys Temperature 030206 dentistry Roughness 050601 international relations Industrial and Manufacturing Engineering 0506 political science Coating 03 medical and health sciences 0302 clinical medicine Surface roughness lcsh:TA401-492 lcsh:Materials of engineering and construction. Mechanics of materials Carrier Composite material |
| Zdroj: | Archives of Foundry Engineering, Vol 16, Iss 3, Pp 83-88 (2016) |
| ISSN: | 2299-2944 |
| Popis: | The influence of the refractory coating which is a mixture of silica flour and kaolin on the surface roughness of the plate castings produced using evaporative patterns had been considered in this work. The kaolin was used as a binder and ratio method was employed to form basis for the factorial design of experiment which led to nine runs of experiments. Methyl alcohol at 99% concentration was used as the carrier for the transfer of the coating to the surface of the patterns. Pouring temperature was observed as a process parameter alongside the mix ratios of the coating. Attempts were made to characterize the refractory coating by using two methods; differential thermal analysis (DTA) and X-ray diffraction. Attempt was also made to characterize the casting material. Gating system design was done for the plate casting to determine the correct proportions of the gating parameters in order to construct the gating system properly to avoid turbulence during pouring of liquid metal. A digital profilometer was used to take the measurements of the surface roughness. It was observed that the mix ratio 90% silica flour-10% kaolin produced the lowest value of the surface roughness of the plate castings and had the lowest material loss in the DTA test. The pouring temperature of 650°C produced best casting. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|