Molhabilidade por PGM-forno matte sintético e industrial
| Autor: | B. M. Thethwayo, Robert Douglas Cromarty |
|---|---|
| Jazyk: | angličtina |
| Rok vydání: | 2015 |
| Předmět: | |
| Zdroj: | Cerâmica, Vol 61, Iss 358, Pp 219-223 (2015) Cerâmica, Volume: 61, Issue: 358, Pages: 219-223, Published: JUN 2015 Cerâmica v.61 n.358 2015 Cerâmica (São Paulo. Online) Universidade de São Paulo (USP) instacron:USP |
| ISSN: | 1678-4553 |
| Popis: | Wettability of SGL's RN-graphite by synthetic and industrial PGM (Platinum Group Metal)-furnace matte (CuFeNiS) was investigated using a sessile drop configuration. This work was done to determine the compatibility of a graphite refractory with liquid PGM-furnace matte. Direct measurements of interfacial contact angles were used to determine wettability. In inert conditions, graphite was poorly wetted by synthetic and industrial PGMfurnace matte (CuFeNiS), the contact angles were > 90° for all tested matte types. No correlation was observed between the sulphur content of the matte and its wetting behaviour. The granulated matte expanded by up to 25 volume % during melting. A molhabilidade do grafite RN-SGL em forno-PGM de acabamento fosco (Cu Fe Ni S) sintético e industrial foi investigada usando uma configuração de gota séssil. Este trabalho foi feito para determinar a compatibilidade de um refratário de grafite com líquido PGM-forno de acabamento fosco. Medidas diretas de ângulos de contato interfacial foram usadas para determinar a molhabilidade. Em condições inertes, grafite foi levemente molhado pelo PGM-forno de acabamento fosco (Cu Fe Ni S) sintético e industrial, os ângulos de contacto foram > 90 ° para todos os tipos de matte testados. Não houve correlação entre o teor de enxofre do acabamento fosco e seu comportamento molhamento. O acabamento fosco granulado foi expandido em até 25% em volume durante a fusão. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|