High-frequency cyclic testing of welded aluminium alloy joints in the region of very high cycle fatigue (VHCF)
| Autor: | H.-J. Christ, Martin Cremer, Martina Zimmermann |
|---|---|
| Přispěvatelé: | Publica |
| Jazyk: | angličtina |
| Rok vydání: | 2013 |
| Předmět: |
Materials science
Welding ultrasonic fatigue testing microstructural variation Industrial and Manufacturing Engineering law.invention Weld seam law Aluminium alloy General Materials Science Longitudinal axis Base metal Joint (geology) very high cycle fatigue Mechanical Engineering Metallurgy technology industry and agriculture Fatigue testing respiratory system Mechanics of Materials Modeling and Simulation visual_art notch effect visual_art.visual_art_medium welded aluminium alloy joints Ultrasonic fatigue |
| Popis: | In the present investigation high-frequency fatigue tests on welded specimens with trimmed surfaces were carried out by means of an ultrasonic fatigue testing system (UFTS). The wave-like distribution of the load amplitude along the longitudinal axis of the UFTS specimens with a maximum in the minimum cross-section (at about the half length) of the sample permits a selective testing of the different weld zones (weld seam, heat-affected zone and base metal). In addition, the influence of microscopic and macroscopic notch effects on the VHCF behaviour was analysed systematically for a precipitation-hardened Al-alloy in different heat-treatment conditions, representing the different zones of a welded joint. “Artificially” notched and heat-treated samples with the same notch factor compared to the weld reinforcement represent the macroscopic notch effect of the welded joint. A comparison of VHCF results of the welded samples with those based on notched specimens is presented and discussed. The weld metal with its various welding defects proved to be the weakest link of the joint structures, provided the reinforcement is trimmed. Welded fatigue samples show the lowest fatigue results in the VHCF regime compared to the base material and heat-affected zone. The VHCF behaviour of artificially notched samples is prone to microstructural effects as could be proven for various heat-treatment conditions. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|