| Popis: |
The microstructure and thermal properties of copolymers of polyethylene terephthalate (PET) containing a crosslinkable terephthalic acid, 1,2-dihydrocyc Iobutabenzene 3,6 dicarboxylic acid (XTA) are reported. Wide angle x-ray scattering (WAXS) show that the addition of XTA does not alter the PET crystal structure in copolymers at low XTA contents. However, the degree of crystallinity drops for higher XTA levels. WAXS profiles show that PET-co-XTA 50% is amorphous, and that PEXTA homopolymer has a different crystal structure. Thermal data from DSC and TGA show that crosslinking of the benzocyclobutene groups (∼350°C) occurs at temperatures between melting (∼250°C) and degradation (∼400°C), making it possible to melt process the copolymers into fibers before the onset of crosslinking. Limiting oxygen index (LOI) measurements show that increased oxygen concentrations are required to sustain a stable flame in PET-co-XTA copolymers; whereas unmodified PET had an LOI value of -18%, the copolymers had LOI values near 32%. Further, while unmodified PET melts and drips as it burns, XTA copolymers formed a stable char that inhibiting flame propagation. An increased char was observed in optical micrographs for XTA containing polymers, and crystalline domains were observed near the burn surface in transmission electron micrographs. |