Synthesis and Characterization of 3-DOM IrO2 Electrocatalysts Templated by PMMA for Oxygen Evolution Reaction
Autor: | Xuechu Sun, Haolin Tang, Jun Yu, Cuicui Li, Fei Liu, Xiu Chen |
---|---|
Jazyk: | angličtina |
Rok vydání: | 2019 |
Předmět: |
Materials science
Polymers and Plastics Electrolysis of water IrO2 catalyst Oxygen evolution chemistry.chemical_element General Chemistry Overpotential water electrolysis Article Catalysis lcsh:QD241-441 Chemical engineering chemistry X-ray photoelectron spectroscopy lcsh:Organic chemistry Rutile OER PMMA template Iridium Mesoporous material |
Zdroj: | Polymers, Vol 11, Iss 4, p 629 (2019) Polymers Volume 11 Issue 4 |
ISSN: | 2073-4360 |
Popis: | Three-dimensional ordered macroporous (3-DOM) IrO2 material was prepared using PMMA as a template and ammonia as a chelator. These 3-DOM IrO2 honeycomb arrays showed a large surface area and ordered macropores (155 nm in diameter) cross-linked by secondary mesopores. Internal structures of 3-DOM IrO2 material were observed microscopically through these secondary pores. According to the X-ray diffraction (XRD) and X-ray photoelectron spectroscopy (XPS) spectra, 3-DOM IrO2 has a rutile crystal structure and is mainly composed of iridium dioxide. In acidic electrolytes, the overpotential of 3-DOM IrO2 material at 0.5 mV cm&minus 2 was only 0.22 V. Accelerated durability tests demonstrated excellent durability of 3-DOM IrO2 as an oxygen evolution reaction (OER) catalyst. |
Databáze: | OpenAIRE |
Externí odkaz: | |
Nepřihlášeným uživatelům se plný text nezobrazuje | K zobrazení výsledku je třeba se přihlásit. |