The influence of Y ion implantation on the oxidation behaviour of ZrN coating
| Autor: | D.R. Wang, X.D. Bai, Yunhan Ling, Q.G. Zhou, X.Y. Xue, Xiaotong Chen, Jie Xu |
|---|---|
| Rok vydání: | 2004 |
| Předmět: |
Materials science
Photoemission spectroscopy Metallurgy Oxide chemistry.chemical_element Yttrium Zirconium nitride engineering.material Condensed Matter Physics Fluence Surfaces Coatings and Films chemistry.chemical_compound Ion implantation chemistry Coating Cathodic arc deposition engineering Composite material Instrumentation |
| Zdroj: | Vacuum. 76:517-521 |
| ISSN: | 0042-207X |
| DOI: | 10.1016/j.vacuum.2004.06.004 |
| Popis: | The purpose of this work was to determine the influence of ion implantation on the oxidation resistance of ZrN coatings. Samples were prepared on AISI 304 stainless steel by cathodic arc deposition. They were submitted to Y implantation at 150 °C with various fluences using a metal vacuum vapour arc ion implanter. The oxidation behaviour of as-deposited and Y-implanted ZrN coatings was characterized by weight gain measurement. The oxidation resistance of the ZrN coating was reduced after it was implanted with yttrium at a low fluence but improved at higher fluence. X-ray photoemission spectroscopy and glancing angle X-ray diffraction were employed to analyze the valence states of the oxide scale and the phase composition of the oxidation layers. Yttrium implantation can greatly improve the oxidation resistance of the ZrN coating. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect