Enhanced Structural, Optical, and Multiferroic Properties of Rod-Like Bismuth Iron Oxide Nanoceramics by Dopant Lanthanum

Autor: Hamed Maleki, Majid Taraz, Asma Mohammadi Badizi, Naimeh Badvi Delfard
Rok vydání: 2019
Předmět:
Zdroj: Journal of Superconductivity and Novel Magnetism. 33:1207-1214
ISSN: 1557-1947
1557-1939
DOI: 10.1007/s10948-019-05294-3
Popis: Herein, the influence of lanthanum concentration on the structural, thermal, optical, ferroelectric, and magnetic properties of Bi1-xLaxFeO3 (BLFO, x = 0, 0.05, 0.1, 0.15, 0.2, and 0.25) nanorods prepared by hydrothermal method was investigated. X-ray diffraction (XRD) and Fourier transform infrared (FTIR) spectroscopy were performed to study the structural properties of BLFO nanoparticles for different lanthanum concentration. The Rietveld refinement and analysis of crystal structure revealed a single-phase perovskite structure with space group R3c. Transmission electron microscope (TEM) image of bismuth iron oxide nanorods exhibits average diameter of ~ 40 nm and length of ~ 2 μm. The ferroelectric Curie temperature of 833 °C (829 °C) was determined for BiFeO3 (Bi0.8La0.2FeO3) by differential thermal analysis (DTA). Diffuse reflectance UV-Vis spectra indicated that the optical band gap is decreased by increasing the lanthanum concentration. The ferroelectric properties of BiFeO3 nanoparticles also improved by adding lanthanum into the structure of bismuth iron oxide. Moreover, J-E curves showed that lanthanum doping can significantly decrease the leakage current of bismuth ferrite nanorods. Finally, vibrating sample magnetometer (VSM) measurements indicated that the weak ferromagnetic behavior is observed for as-prepared BLFO nanorods with x ≤ 0.15. However, for the 20 mol% lanthanum doping, a magnetic transition from weak ferromagnetic to antiferromagnetic occurred.
Databáze: OpenAIRE
Externí odkaz: