| Autor: |
Kamarudin Hussin, Haider T. Naeem, Nurhuda Bashirom, Azim Rahmat, Kahtan S. Mohammad |
| Rok vydání: |
2015 |
| Předmět: |
|
| Zdroj: |
AIP Conference Proceedings. |
| ISSN: |
0094-243X |
| DOI: |
10.1063/1.4915743 |
| Popis: |
In this study, influence cobalt additives on the microstructural and hardness properties of an Al-Zn-Mg-Cu-Fe-Cr-Ni PM alloy undergone the retrogression and re-aging treatment were carried out. Green compacts pressed at 370 MPa were then sintered at temperature 650°C in argon atmosphere for two hours. The sintered compacts subjected to a homogenizing treated at 470°C for 1.5 hours then aged at 120°C for 24 hours and retrogressed at 180°C for 30 minutes, and then re-aged at 120°C for 24 hours. Microstructural results of the Al-Zn-Mg-Cu-Fe-Cr-Ni-Co alloys introduced an intermetallics compound in the matrix of alloy, identified as the Al5Co2, Al70Co20Ni10 and Al4Ni3 phases besides to the MgZn2 and Mg2Zn11 phases which produced of the precipitation hardening during heat treatment. These compounds with precipitates provided strengthening of dispersion that led to improved Vickers’s hardness and dinsifications properties of the alloy. The highest Vickers hardness of aluminum alloy containing cobalt was gotten a... |
| Databáze: |
OpenAIRE |
| Externí odkaz: |
|