Laser composite surfacing of AISI 304 stainless steel with titanium boride for improved wear resistance
| Autor: | J. Dutta Majumdar, Indranil Manna, B. Ramesh Chandra |
|---|---|
| Rok vydání: | 2007 |
| Předmět: |
Materials science
Mechanical Engineering Composite number Metallurgy Abrasive chemistry.chemical_element Surfaces and Interfaces Laser Surfaces Coatings and Films law.invention chemistry.chemical_compound Hexafluoride chemistry Mechanics of Materials law Volume fraction Irradiation Adhesive Titanium |
| Zdroj: | Tribology International. 40:146-152 |
| ISSN: | 0301-679X |
| Popis: | The present study concerns development of a hard in situ boride-dispersed composite layer on the surface of AISI 304 stainless steel substrate to improve the wear resistance property. Laser processing was carried out by melting the surface of sand-blasted AISI 304 stainless steel substrate using a continuous wave CO 2 laser and simultaneous deposition of a mixture of K 2 TiF 6 (potassium titanium hexafluoride) and KBF 6 (potassium hexafloroborate) (in the weight ratio of 2:1) using Ar as shrouding environment. Powder feed rate was maintained constant at 4 g/min. Irradiation results in dissociation of a pre-deposited mixture along with a part of the stainless steel substrate, intermixing and rapid solidification to form the composite layer on the surface. The micro-structure of composite layer consists of dispersion of titanium boride particles in AISI 304 stainless steel matrix. Volume fraction of particles is found to be uniform throughout the composite layer, though varied with laser parameters. The micro-hardness of the surface was improved 250-350 VHN as compared to 220 VHN of the AISI 304 stainless steel substrate with a significant improvement in wear resistance property. The mechanism of wear was found to be a combination of adhesive and abrasive in as-received stainless steel. However, it was predominantly abrasive for laser composite surfaced stainless steel. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect