Interfacial reactions between nickel thin films and GaN
| Autor: | B. P. Luther, S. D. Wolter, Suzanne E. Mohney, Hari S. Venugopalan, Joan M. Redwing |
|---|---|
| Rok vydání: | 1997 |
| Předmět: | |
| Zdroj: | Journal of Applied Physics. 82:650-654 |
| ISSN: | 1089-7550 0021-8979 |
| Popis: | Thin Ni films on GaN were annealed at temperatures between 400 and 900 °C in N2, Ar, and forming gas and were analyzed using glancing angle x-ray diffraction and Auger depth profiling. The first indication of an interfacial reaction was found after an anneal at 600 °C for 1 h, after which Ga was observed to be dissolved in the face-centered cubic Ni film. The extent of dissolution increased with continued annealing. After annealing at 750 °C for 1 hr in either N2 or Ar, greater intermixing occurred. The reaction product was either Ni3Ga or face-centered cubic Ni with dissolved Ga. Annealing at 900 °C resulted in the formation of the B2 phase NiGa. It was clear from Auger depth profiles that the reacted film contained significantly more Ga than N and that N2 gas was released to the annealing environment, even when the samples were annealed in N2 gas at 1 atm. Thus, a trend of increasing Ga content in the reacted films was observed with increasing temperature. The observed reactions are consistent with the ... |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|