Synthetic Condition and Properties of the BiPbSrCaCuO Superconductor with Single High-Tc Phase

Autor: Yuping Sun, J.J. Du, Jianyi Jiang, Fanchun Zeng, Huaqing Yin
Rok vydání: 1990
Předmět:
Zdroj: physica status solidi (a). 119:555-560
ISSN: 1521-396X
0031-8965
Popis: The single 110 K phase Bi-PbSrCaCuO superconductor is prepared by multi-grinding and sintering in air. The forming process of 110 K phase is discussed. The properties of the samples obtained by using different synthetic condition are studied. The results indicate that the grains of the high-Tc phase may grow on the surface of the grain of the low-Tc phase and that the forming rate of the high-Tc phase can be speeded by multi-grinding. The step of χ′ and the peak of χ″ about 100 K are observed in the multigrinding sample in terms of the ac complex susceptibility χ′-iχ″. The step and the peak may be caused by the weak-link. Der Einphasen-110 K-BiPbSrCaCuO-Supraleiter wird mittels Mehrfachmahlen und Sinterung in Luft hergestellt. Der Formierungsprozes der 110 K-Phase wird diskutiert. Unterschiede der unter verschiedenen Synthetisierungsbedingungen erhaltenen Proben werden untersucht. Die Ergebnisse zeigen, das die Korner der Hoch-Tc-Phase auf der Oberflache des Korns der Nieder-Tc-Phase wachsen konnen, und das die Bildungsgeschwindigkeit der Hoch-Tc-Phase durch Mehrfachmahlen erhoht werden kann. Die Stufe von χ′ und das χ″-Maximum bei etwa 100 K werden in den mehrfach gemahlenen Proben mit der komplexen Wechselspannungssuszeptibilitat χ′-iχ″ beobachtet. Die Stufe und das Maximum konnen durch die schwache Verbindung verursacht werden.
Databáze: OpenAIRE
Externí odkaz: