Highly gas permeable, ultrathin Teflon AF2400/γ-alumina composite hollow fiber membranes for dissolved gas analysis
| Autor: | Chuan Chen, Chien-Hua Chen, Y.S. Lin, Liang-Chih Ma, Sainan Liu |
|---|---|
| Rok vydání: | 2017 |
| Předmět: |
Chromatography
Materials science Transformer oil Dissolved gas analysis Composite number Filtration and Separation 02 engineering and technology engineering.material 010402 general chemistry 021001 nanoscience & nanotechnology 01 natural sciences Biochemistry 0104 chemical sciences γ alumina Membrane Chemical engineering Coating engineering General Materials Science Composite membrane Physical and Theoretical Chemistry 0210 nano-technology Mesoporous material |
| Zdroj: | Journal of Membrane Science. 540:243-250 |
| ISSN: | 0376-7388 |
| Popis: | Dissolved gas analysis (DGA) is a useful approach to monitor the electrical faults of transformers. For extraction of dissolved gases from transformer oil in the DGA process, membrane-based separation represents an appealing technology option since the use of an oil-resistant, stable and highly gas permeable dense membrane can greatly enhance the efficiency by shortening the extraction time. However, most membranes reported in the literature have a membrane thickness in the micrometer range, making these membrane devices not sufficiently effective in practical separation of dissolved gasses from transformer oil. To reduce the thickness of membranes, Teflon AF2400 composite membranes synthesized using three different types of alumina (Al2O3) supports were investigated, including macroporous α-Al2O3 disk support, macroporous α-Al2O3 hollow fiber support, and mesoporous γ-Al2O3/α-Al2O3 hollow fiber support. The result shows that the γ-Al2O3/α-Al2O3 supports with a mesoporous top-coating γ-Al2O3 layer prepared by the sol-gel method could provide a high-quality surface for synthesizing an ultrathin and defect-free Teflon AF2400 layer. For the ultrathin Teflon AF2400/γ-Al2O3 composite hollow fiber membranes prepared by coating with a 0.5 wt% Teflon AF2400 solution, the thickness of the Teflon AF2400 layer is about 270 nm, and the permeances of H2, CH4, CO2 and C2H6 at room temperature can reach to 14,069, 2847, 11,901 and 2030 GPU, respectively, which are about 8 times higher than that of the α-Al2O3 disk or hollow fiber supported membranes. This result demonstrates the promise of the ultrathin Teflon AF2400/γ-Al2O3 composite hollow fiber membranes for extraction of dissolved gases from the transformer oil for DGA. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect