| Popis: |
Previous work has shown that rolling of an extruded Cu–8Cr–4Nb (GRCop-84) alloy results in higher steady-state creep rates over a range of stresses, leading to concern that other post-processing methods could have substantial deleterious effects on creep properties. To explore that possibility, constant-stress creep tests were conducted at 773 K on rolled GRCop-84 after it was subjected to either friction stir welding (FSW) or a 24 h 1073 K simulated-life heat treatment. The FSW had no measurable effect on the creep rate of the rolled material, but did have detrimental effects on the creep ductility caused by softening, and thus strain localization, in the heat-affected zone of the weld. The simulated-life heat treatment decreased the steady-state creep rate by approximately 45% as compared to the rolled material, leading to longer creep life at a particular applied stress. Electron backscatter diffraction methods were used to compare the microstructural features of extruded, rolled and annealed material forms. It was determined that the rolling procedure decreased the grain size, and decreased the intensity of the texture as compared to the extruded form. The simulated-life heat treatment allowed for the substantial development of twins along with minor grain growth, and a substantial decrease in texturing. |
Full Text from ScienceDirect