Microwave dielectric properties of BaO–ZnO–B2O3–P2O5 glass–ceramic for LTCC application

Autor: Juan Xi, J. Huang, Zhou Changrong, Baobiao Lu, Fei Shang, Jiwen Xu, J. J. Chen, Denghui Jiang, C. L. Yuan, G. H. Chen
Rok vydání: 2019
Předmět:
Zdroj: Journal of Materials Science: Materials in Electronics. 30:18599-18605
ISSN: 1573-482X
0957-4522
DOI: 10.1007/s10854-019-02212-0
Popis: A new 10BaO–40ZnO–15B2O3–35P2O5 (wt%) glass–ceramic with ultra-low permittivity and excellent thermal stability were fabricated by solid-state reaction method. The sintering, phase composition, microstructure and microwave dielectric properties of the glass–ceramics were studied through XRD, SEM, density and dielectric property measurement. The result shows BaZn2(PO4)2 precipitates first at low sintering temperature of 550 °C, and with increasing sintering temperature, Zn3(PO4)2 and Zn3(BO3)2 phases come out in succession in the glass. The bulk densities of the glass–ceramics firstly increase and then decrease with the increment of firing temperature and the highest density can be achieved at 700 °C. The glass–ceramics sintered at 700 °C for 2.5 h possesses the optimal dielectric properties of er = 4.16, Q × f = 12,250 GHz (13.6 GHz), and τf = − 1.5 ppm/°C. Moreover, the samples have good chemical compatibility with silver electrodes, which indicates that the developed glass–ceramic materials are suitable for LTCC applications.
Databáze: OpenAIRE