High cycle fatigue behaviors of API X65 pipeline steel welded joints in air and H2S solution environment
| Autor: | Quanjun Xu, Caiyan Deng, Baoming Gong, Dongpo Wang, Zhiwei Gao, Yang Yu |
|---|---|
| Rok vydání: | 2021 |
| Předmět: |
Austenite
Heat-affected zone Materials science Renewable Energy Sustainability and the Environment Bainite Energy Engineering and Power Technology 02 engineering and technology 010402 general chemistry 021001 nanoscience & nanotechnology Condensed Matter Physics 01 natural sciences 0104 chemical sciences Stress (mechanics) Fuel Technology Martensite Composite material 0210 nano-technology Stress concentration Hydrogen embrittlement Electron backscatter diffraction |
| Zdroj: | International Journal of Hydrogen Energy. 46:10423-10437 |
| ISSN: | 0360-3199 |
| DOI: | 10.1016/j.ijhydene.2020.12.140 |
| Popis: | To investigate the mutual effect of hydrogen, microstructures and stress concentration on the fatigue failure, fatigue behaviors of X65 steel welded joints in both air and saturated H2S solution were investigated at high cycle regime. The experimental result demonstrates that due to lower dislocation density observed by electron backscattered diffraction (EBSD), the fine grain heat affected zone (FGHAZ) is prone to induce cyclic strain localization and further lead to fatigue crack propagating along the FGHAZ in air. Furthermore, the quasi-cleavage with brittle-like fatigue striations and secondary crack on the fracture surface in saturated H2S solution is attributed to hydrogen embrittlement. Moreover, compared with base metal (BM) and FGHAZ, the weld metal (WM) and coarse grain heat affected zone (CGHAZ) are composed of bainite and martensite/austenite (M/A) phase, and more sensitive to hydrogen. Therefore, the fatigue crack is prone to grow along the interface between WM and CGHAZ under the normal applied stress. |
| Databáze: | OpenAIRE |
| Externí odkaz: |
|
Full Text from ScienceDirect