Modélisation multiphysique des mécanismes de formation de la phase blanche (white etching layer)
| Autor: | Thiercelin, Léo |
|---|---|
| Přispěvatelé: | Laboratoire de Mécanique et d'Acoustique [Marseille] (LMA ), Aix Marseille Université (AMU)-École Centrale de Marseille (ECM)-Centre National de la Recherche Scientifique (CNRS), Laboratoire de Mécanique des Contacts et des Structures [Villeurbanne] (LaMCoS), Institut National des Sciences Appliquées de Lyon (INSA Lyon), Institut National des Sciences Appliquées (INSA)-Université de Lyon-Institut National des Sciences Appliquées (INSA)-Université de Lyon-Centre National de la Recherche Scientifique (CNRS), L'Institut de Recherche Technologique (IRT) de la filière Ferroviaire (IRT Railenium), Université Polytechnique Hauts-de-France (UPHF), Aix Marseille Université, Frédéric Lebon, Aurélien Saulot, Université de Lyon-Institut National des Sciences Appliquées (INSA)-Université de Lyon-Institut National des Sciences Appliquées (INSA)-Centre National de la Recherche Scientifique (CNRS) |
| Jazyk: | francouzština |
| Rok vydání: | 2021 |
| Předmět: |
contact roue-rail
modèle thermomécanique phase change phase blanche plasticité thermomechanical modelling Transformation Tribologique de Surface (TTS) experiments [SPI.MECA.SOLID]Engineering Sciences [physics]/Mechanics [physics.med-ph]/Solid mechanics [physics.class-ph] Tribological Surface Transformation (TST) wheel-rail contact changement de phase essais plasticity calculs par éléments finis White Etching Layer (WEL) Finite Elements simulations |
| Zdroj: | Mécanique des solides [physics.class-ph]. Aix Marseille Université, 2021. Français Mécanique des solides [physics.class-ph]. Aix Marseille Université, 2021. Français. ⟨NNT : ⟩ |
| Popis: | Tribological Surface Transformations (TST), known as White Etching Layer (WEL) in the wheel-rail contact, correspond to progressive and irreversible transformations on the rail surface that can lead to cracking and then failure of the rails. These areas of nanocrystalline structures are made up of several phases which show severe plastic deformation and temperature rises (which can exceed the austenitization temperature). A scenario of progressive formation of WELs has been proposed by introducing stages of microstructure evolution in the case of pearlitic steels used in railways. These stages are defined by indicators obtained by a multi-scale observations method (optical analyses and EBSD). A thermomechanical model taking into account a coupling between hydrostatic pressure, shear stress and temperature is presented. 2-D finite element simulations representative of the wheel-rail contact conditions have successfully qualitatively reproduced WEL spots. This model is also able to capture the effects of the rail dynamics on the formation kinetics of WEL, which could explain the sparsely scattered formation of WEL by island.Representative tests of wheel-rail contact conditions were carried out to validate the role of shear stress in WEL formation. On the one hand, cyclic tests of pure shear under controlled temperature ("hat-shaped" specimen) were carried out using the GLEEBLE thermomechanical simulator (Mateis-LaMCoS, INSA Lyon). On the other hand, “roller on circular rail” experiments (Triboring test rig, LaMCoS, INSA Lyon) were performed to determine the pressure-shear coupling.; Un scénario de formation progressive des WEL a été proposé par l’introduction de stades d’évolution de la microstructure dans le cas d’aciers perlitiques utilisés dans le ferroviaire. Ces stades se définissent par des indicateurs obtenus par une méthode d’observations multi-échelles (analyses optiques et EBSD). Un modèle thermomécanique prenant en compte un couplage entre pression hydrostatique, cisaillement et température est présenté. Des simulations 2-D par éléments finis représentatives des conditions du contact roue-rail ont permis de reproduire qualitativement des zones de WEL. Ce modèle est de même capable de rendre compte des effets de la dynamique ferroviaire sur la cinétique de formation de WEL qui pourrait plus particulièrement expliquer la formation éparse de WEL par ilot.Des essais représentatifs des conditions du contact-roue rail ont été effectués pour valider le rôle du cisaillement dans la formation de WEL. D’une part, des essais cycliques de cisaillement pur sous température contrôlée (éprouvette « chapeau ») ont été réalisés en utilisant le simulateur thermomécanique GLEEBLE (Mateis-LaMCoS, INSA Lyon). D’autre part, des essais de type galet sur rail circulaire (banc Triboring, LaMCoS, INSA Lyon) ont été menés pour déterminer le couplage pression-cisaillement. |