| Abstrakt: |
Hot rolling of beams is carried out essentially in two stages. Roughing is performed in a reversing mill at temperatures in the range of 1100 oC, at relatively low strain rates and with long interpass times. Finishing is carried out in a reversing two stand mill at temperatures in between 1000 and as low as 700 oC considering parts of the web in the last passes. Strain rates are moderate and interpass times are in the range of 5 to 20s. There is, therefore, as it can be seen from the description just made of the rolling schedule, a fair resemblance to deformation in plate mills. Technology for themomechanical processing, TMP, of plates is very well known and disseminated. Application of this technology to beam rolling is, on the other hand, rather seldom known of. This paper addresses an application of TMP plate technology to beam rolling. In particular, austenite grain size evolution is examined. The usage of Nb microalloyed steels to this process is discussed in terms of possible beneficial effects to ferrite grain refinement. |