| Autor: |
Duarte, Marcia Adriana Tomaz, Coppini, Larissa, Lucchesi, C., Macedo, Marcelo, Duek, Eliana Aparecida De Rezende |
| Zdroj: |
Materials Science Forum; November 2012, Vol. 730 Issue: 1 p50-55, 6p |
| Abstrakt: |
The use of bioabsorbable polymers in biomedical application has increased greatly in recent years due to their good compatibility and bio-reabsorption. To obtain a polymeric material suitable for medical applications, the obtention and characterization of copolymer poly (L-co-DL lactic acid) (PLDLA) with the addition of poly (caprolactone triol) (PCL-T) was studied. PLDLA/PCL-T membranes were prepared by solvent casting in the 100/0, 90/10 and 70/30 (w/w) compositions. The membranes were characterized by Atomic Force Microscopy (AFM), Cellular Adhesion and Energy Dispersed Spectroscopy (EDS). Using MFA it was observed that an addition of PCL-T contributes to rough morphology and greater porosity. Increased cell adhesion on 90/10 and 70/30 membranes compared to 100/0 composition and controls was observed. From these results, it was observed that PCL-T improved cellular adhesion of the PLDLA membrane when compared to membranes without PCL-T. The PLDLA/PCL-T membrane is indicated for use in medical devices which do not require long implantation time, such as support for cell culture, dressings for skin ulceration and guided regeneration in periodontics. |
| Databáze: |
Supplemental Index |
| Externí odkaz: |
|