| Autor: |
Andrievskii, R., Zeer, S., Ganelin, V., Lapovok, V., Trusov, L., Shumanova, S. |
| Zdroj: |
Soviet Powder Metallurgy & Metal Ceramics; 1985, Vol. 24 Issue 2, p111-115, 5p |
| Abstrakt: |
As a result of oxidation of compacts from nickel and copper UFPs, their electrical resistivities may vary within a wide range. During the vacuum sintering of nickel and copper UFPs changes in electrical resistivity are recorded before densification. During heating the electrical resistivity of compacts may fall at a rate of up to half an order a minute. Measurements of γ and δL/L during repeated heating-and-cooling cycles reveal increases in the electrical resistivity and elongation of specimens, which may be linked with elastic after-effect phenomena. A small rise in electrical resistivity during heating to 100‡C may also be brought about by elastic stress relaxation. An increase in electrical resistivity accompanied by shrinkage during a rise in temperature after isothermal sintering is indicative of rupture of contacts during densification; the extent of this process, which may be linked with sliding of whole particles relative to one another, diminishes with rise in temperature. [ABSTRACT FROM AUTHOR] |
| Databáze: |
Complementary Index |
| Externí odkaz: |
|