Partially degradable friction-welded pure iron-stainless steel 316L bone pin.

Autor: Nasution AK; Faculty of Biosciences and Medical Engineering, Universiti Teknologi Malaysia, Johor Bahru, 81310, Malaysia; Faculty of Engineering, Muhammadiyah University of Riau, Pekanbaru, Indonesia., Murni NS, Sing NB, Idris MH, Hermawan H
Jazyk: angličtina
Zdroj: Journal of biomedical materials research. Part B, Applied biomaterials [J Biomed Mater Res B Appl Biomater] 2015 Jan; Vol. 103 (1), pp. 31-8. Date of Electronic Publication: 2014 Apr 23.
DOI: 10.1002/jbm.b.33174
Abstrakt: This article describes the development of a partially degradable metal bone pin, proposed to minimize the occurrence of bone refracture by avoiding the creation of holes in the bone after pin removal procedure. The pin was made by friction welding and composed of two parts: the degradable part that remains in the bone and the nondegradable part that will be removed as usual. Rods of stainless steel 316L (nondegradable) and pure iron (degradable) were friction welded at the optimum parameters: forging pressure = 33.2 kPa, friction time = 25 s, burn-off length = 15 mm, and heat input = 4.58 J/s. The optimum tensile strength and elongation was registered at 666 MPa and 13%, respectively. A spiral defect formation was identified as the cause for the ductile fracture of the weld joint. A 40-µm wide intermetallic zone was identified along the fusion line having a distinct composition of Cr, Ni, and Mo. The corrosion rate of the pin gradually decreased from the undeformed zone of pure iron to the undeformed zone of stainless steel 316L. All metallurgical zones of the pin showed no toxic effect toward normal human osteoblast cells, confirming the ppb level of released Cr and Ni detected in the cell media were tolerable.
(© 2014 Wiley Periodicals, Inc.)
Databáze: MEDLINE
Externí odkaz: