Influence of implant drill materials on wear, deformation, and roughness after repeated drilling and sterilization.

Autor:	Batista Mendes GC; Former Masters Degree Student of Latin American Institute of Dental Research and Education (ILAPEO), Curitiba, Brazil. †Professor, Latin American Institute of Dental Research and Education (ILAPEO), Curitiba, Brazil. ‡Phd Student, Oral and Maxillofacial Department, São Paulo State University, Araçatuba, Brazil. §Professor, Latin American Institute of Dental Research and Education (ILAPEO), Curitiba, Brazil., Padovan LE, Ribeiro-Júnior PD, Sartori EM, Valgas L, Claudino M
Jazyk:	angličtina
Zdroj:	Implant dentistry [Implant Dent] 2014 Apr; Vol. 23 (2), pp. 188-94.
DOI:	10.1097/ID.0000000000000028
Abstrakt:	Purpose: The aim of this study was to evaluate deformation, roughness, and mass loss of stainless steel, diamond-like carbon (DLC)-coated and zirconia drills after multiple osteotomies with sterilization procedures. Materials and Methods: Drilling procedures were performed using stainless steel (G1), DLC-coated (G2), and zirconia (G3) drills. All groups were divided in subgroups 1, 2, 3, 4, and 5, corresponded to drills used 0, 10, 20, 30, and 40 times, respectively. Results: No significant differences in mass and roughness were detected among all groups and subgroups. In SEM images, all groups revealed signs of wear while coating delamination was detected in G2. Drills from G1 displayed more irregular surface, whereas cutting edges were more regular in G3. Conclusion: Zirconia drills presented more regular surfaces whereas stainless steel drills revealed more severe signs of wear. Further studies must be performed to evaluate the putative influence of these findings in heat generation.
Databáze:	MEDLINE
Externí odkaz:	Zobrazit plný text záznamu