Publikováno v:
Nuclear Engineering and Technology, Vol 56, Iss 7, Pp 2584-2594 (2024)
A novel approach to incorporating oxide formers into ferritic ODS production has been developed using the co-precipitation technique. This method enables the tailored design of complex nano-oxides, integrated during Mechanical Alloying (MA) and preci
Externí odkaz:
https://doaj.org/article/6317f05d14fc4e6fbe07987bccc83be9
Publikováno v:
Materials Reports: Energy, Vol 4, Iss 4, Pp 100297- (2024)
This study investigates the impact of silicon (Si) on the corrosion resistance and post-corrosion toughness of ferrite/martensitic (F/M) steels in a liquid lead-bismuth eutectic (LBE) environment. Corrosion tests were performed on HT-9 and EP-823 (1.
Externí odkaz:
https://doaj.org/article/32479d0956fe4897bac0ccb8f735491d
Publikováno v:
Journal of the Mechanical Behavior of Materials, Vol 33, Iss 1, Pp 391-9 (2024)
Herein, fatigue and crack propagation tests were conducted using the small-punch-fatigue (SPF) test to verify its applicability to assess fatigue strength and fatigue crack propagation behavior. During the SPF test, a fatigue crack first initiated at
Externí odkaz:
https://doaj.org/article/c44b11f4ac514cf283a82b5d37b42395
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Autor:
Eberhard Altstadt, Frank Bergner, Jann-Erik Brandenburg, Paul Chekhonin, Jakub Dykas, Mario Houska, Andreas Ulbricht
Publikováno v:
Frontiers in Nuclear Engineering, Vol 3 (2024)
Neutron irradiation causes embrittlement of reactor pressure vessel (RPV) steels. Post-irradiation annealing is capable of partly or fully restoring the unembrittled condition. While annealing at high temperatures (e.g., 475°C) was successfully appl
Externí odkaz:
https://doaj.org/article/0378eacb0ea049799b61a394522c5f11
Autor:
Borja Arroyo, Laura Andrea, José A. Álvarez, Sergio Cicero, Federico Gutiérrez-Solana, Luis Abarca
Publikováno v:
Metals, Vol 14, Iss 11, p 1234 (2024)
The present work is a relevant advance in the validation of the incremental step loading technique (ASTM F1624 standard) when applied to Small Punch tests (SPT) for the threshold load determination of medium- and high-strength steels in aggressive en
Externí odkaz:
https://doaj.org/article/41de7ea38861450fbab81f1afdb078eb
Publikováno v:
Journal of Materials Research and Technology, Vol 27, Iss , Pp 733-756 (2023)
Four types of iron-chromium-aluminum (FeCrAl) alloys, composed of different elements, were used to investigate the creep performance and high-temperature oxidation resistance. The microstructures in the undeformed regions after the small punch creep
Externí odkaz:
https://doaj.org/article/125cbc726e3a4b6b9a08683ffb89e7c9
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Publikováno v:
Metals, Vol 14, Iss 10, p 1104 (2024)
The utilization of micro-sample testing has demonstrated its effectiveness in conducting quantitative research on mechanical properties, damage evolutions and fracture features. For in-service equipment, millimicron sampling allows for non-destructiv
Externí odkaz:
https://doaj.org/article/1e500108d1564c5896d200d66eb8ab59