Publikováno v:
High Temperature Materials and Processes, Vol 41, Iss 1, Pp 523-530 (2022)
In this study, the ductile iron ingots are cast using a metal mold, and the riser neck diameter is changed to control the micro-shrinkage porosity, which can affect the ultra-low temperature toughness of ferritic ductile iron. The metallographic stru
Externí odkaz:
https://doaj.org/article/892f7d70bfdc4c11a629f9a729d13e18
Autor:
Wenjie Wang, Zekun Wang, Zhiren Sun, Zhou Zhou, Kai Zhang, Li Ma, Yuwei Wang, Sen Yang, Zherong Huang, Kaikun Wang
Publikováno v:
Materials Research Express, Vol 11, Iss 1, p 016511 (2024)
This study characterizes the fractography of ferritic ductile iron under various loads, including tensile, fatigue and bending, and impact conditions. The results indicate that ductile fracture is the primary mechanism observed during tensile testing
Externí odkaz:
https://doaj.org/article/4a9a7539df7a42fd8f5a6876e3bcac41
Publikováno v:
Archives of Metallurgy and Materials, Vol vol. 67, Iss No 3, Pp 999-1005 (2022)
Two standardised grades of spheroidal cast iron determined in standard EN PN 1563 – 1997 as: EN-GJS-350 – 22LT (T = –40°C) and EN GJS 400 – 18LT (T = –20°C) are intended for work at low temperatures: –20 and –40oC. The main mechanical
Externí odkaz:
https://doaj.org/article/99b493a2a45e4712b6046c82fbd9df07
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Publikováno v:
China Foundry, Vol 10, Iss 3, Pp 141-147 (2013)
Casting defects could largely affect the mechanical properties of casting products. A number of test pieces made of ductile iron (EN-GJS-400-18-LT) with different levels of shrinkage porosity were prepared and then tensile and fatigue tests were perf
Externí odkaz:
https://doaj.org/article/65928119500e407499580e1a374f1d52
Autor:
Çetin Melik
Publikováno v:
High Temperature Materials and Processes, Vol 30, Iss 1-2, Pp 87-98 (2011)
Wear behaviour of special brass produced through two different methods (centrifugal and sand casting) was investigated. The wear tests were carried out at sliding velocities of 0.2 ms–1, 0.3 ms–1, 0.4 ms–1 and 0.5 ms–1 and under 10 N, 20 N, a
Externí odkaz:
https://doaj.org/article/531661d6d76d4c6897cbed6d315e6022
Publikováno v:
Metals, Vol 9, Iss 1, p 24 (2018)
Microstructural, mechanical, and fatigue properties of solution strengthened ferritic ductile iron have been evaluated as functions of different solidification times. Three types of cast samples with increasing thickness have been produced in a green
Externí odkaz:
https://doaj.org/article/1a10f87f303547c6b820990743c4dab6
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.