Nihon Kikai Gakkai ronbunshu, Vol 83, Iss 855, Pp 17-00273-17-00273 (2017)
There are many studies reported that a fatigue crack propagated in a tensile mode macroscopically and the fracture surface was mainly occupied by striations in many metals. Whereas, a unique fracture in which a crack propagated in a macroscopic shear
Externí odkaz:
https://doaj.org/article/60724a0b2e654c78b829f3c12e3889f5
Publikováno v:
Nihon Kikai Gakkai ronbunshu, Vol 83, Iss 855, Pp 17-00274-17-00274 (2017)
Fatigue cracks in some aluminum alloys propagate not in a typical tensile mode with striations but in a macroscopic shear direction with ductile facets under specific conditions. In the previous paper, it was shown that this unique propagation of a s
Externí odkaz:
https://doaj.org/article/a2eb2d11b88e4a5f8c6d672ebd736a08
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Kniha
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.