Transactions of Nonferrous Metals Society of China. 23:625-630
The multi-pass hot compression test of 7055 aluminum alloy was performed at different temperatures and then the samples were heat treated by T6 heat treatment. The compressed samples were analyzed by OM and TEM. The results reveal that the average as
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::48181cdbf7274c6a9dc44641b70dde63
https://doi.org/10.1016/s1003-6326(13)62508-x
https://doi.org/10.1016/s1003-6326(13)62508-x
Publikováno v:
Rare Metals. 29:426-432
Compression tests of the Al-Zn-Mg-Cu-Zr(7055) alloy were performed at various strains and temperatures from 300 to 450°C under a constant strain rate between 10−2 s−1 and 1 s−1. Microstructures during hot deformation were studied by transmissi
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::401a3b91475fe501e856ac9befaf2fc0
https://doi.org/10.1007/s12598-010-0143-y
https://doi.org/10.1007/s12598-010-0143-y
Publikováno v:
Materials Science Forum. 650:295-301
Compression tests were performed at temperatures from 350 to 450 °C with different strain rates of 1.0×10−2 and 1.0×10−1 s−1. The microstructures of deformed samples were investigated by electron backscatter diffraction (EBSD). Microstructur
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::d91977eef6341c9cedbe737d65d5631a
https://doi.org/10.4028/www.scientific.net/msf.650.295
https://doi.org/10.4028/www.scientific.net/msf.650.295
Publikováno v:
International Journal of Minerals, Metallurgy, and Materials. 17:46-52
The hot deformation behavior and microstructures of Al-7055 commercial alloy were investigated by axisymmetric hot compression at temperatures ranging from 300°C to 450°C and strain rates from 10−2 to 10 s−1, respectively. Microstructures of de
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::24ab1c7695cb754f2f28f3706cbac23a
https://doi.org/10.1007/s12613-010-0108-z
https://doi.org/10.1007/s12613-010-0108-z
Autor:
Zhou, Bing Li, Zhang, Qun
Publikováno v:
Advanced Materials Research; September 2012, Vol. 566 Issue: 1 p591-596, 6p