Publikováno v:
Applied Mechanics and Materials. 251:351-354
The difference in microstructures and properties of 600MPa cold rolled dual phase steel with the different composition had been studied in this paper. It can be noticed that the Si-Mn-Cr steel have finer ferrite and more martensite whose content is a
Publikováno v:
Advanced Materials Research. :464-467
A measurement method for magnetic property of the non-oriented silicon steels WD23 and WD20 by X-ray diffraction (XRD) has been introduced. The measurement results show that this method is simple and the size(amount) of the required sample is small.
Publikováno v:
Applied Mechanics and Materials. :471-475
The multi-pass compression deformation of low carbon bainitie steel was carried out on a thermal simulator between a temperature range of 1050~800°Cwith accumulated 60.7% deformation and a deformation rate of 2s-1. The recrystallization behavior of
Publikováno v:
Advanced Materials Research. 586:225-229
The variation rules of strength with the microstructure and precipitates of container steel were studied by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The results show that the microstructu
Influence of Microstructure and Precipitates on the Mechanical Properties of High Strength Hot Strip
Publikováno v:
Advanced Materials Research. :1678-1682
The relation between the microstructure, precipitates and the longitudinal mechanical properties of high strength hot strip was studied by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM). The res
Publikováno v:
Advanced Materials Research. :645-649
The microstructure and precipitates of the V-N microalloyed steels whose carbon content were respectively 0.27% and 0.35%, were investigated by scanning electron microscope (SEM) and transmission electron microscope (TEM). It is shown that the micros
Publikováno v:
Advanced Materials Research. :1669-1674
The morphology of inhibition layer and adhesion of Zn coating about a 600MPa grade high Al dual phase steel were studied by grow discharge spectrometry (GDS), scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The results
Publikováno v:
Advanced Materials Research. :1169-1173
An original 600MPa high aluminum galvanized dual phase steel had been successfully developed in this paper. The microstructure analysis showed that the microstructures of the steel mainly consist of ferrite and 8%~11% martensite as well as 4%~6% reta