Elena Murashova, Alexander Yaroslavtsev, Denis Leshchev, Yu. D. Seropegin, Zh. M. Kurenbaeva, Anna Tursina, Dariusz Kaczorowski, E.V. Marushina
Publikováno v:
Journal of Alloys and Compounds. 580:55-60
The intermetallic phase Ce 2 RuAl was synthesized by arc melting the elemental components and subsequent annealing of the product at 823 K. Its crystal structure was determined from the single-crystal X-ray diffraction data and confirmed by powder X-
Publikováno v:
Journal of Alloys and Compounds. 577:677-682
We report on the synthesis, crystallographic analysis, and physical properties of the new intermetallic compound CePd4Sn. It crystallizes in the orthorhombic Cmce space group with cell dimensions a = 9.003(4) angstrom, b = 23.613(3) angstrom, c = 8.2
Publikováno v:
Journal of Solid State Chemistry. 200:7-12
Crystal structures of three members of a unique homological series with the general formula CemPdnIn3m+2n based on the AuCu3 and PtHg2 structure types were studied by single-crystal X-ray diffraction. The compounds crystallize with space group P4/mmm
Publikováno v:
Intermetallics. 32:194-199
A new compound ErPt4In4 was synthesized by arc melting and its crystal structure was determined from the single crystal X-ray diffraction data: space group P63/mmc, a = 4.5321(9) A, c = 19.807(13) A, Pearson symbol hP18. The new structure type is com
Publikováno v:
Journal of Alloys and Compounds. 526:125-128
The crystal structure of the novel compound Ce 3 Rh 5 Si was solved by means of powder diffraction pattern analysis using the charge-flipping method. The refinements yielded the space group Pnma and the orthorhombic unit cell parameters: a = 1.52632(
Publikováno v:
Journal of Alloys and Compounds. 509:8987-8990
The crystal structure of the novel compound Yb3Pt23Si11 has been determined from powder X-ray diffraction data to be isotypic with cubic Ce3Pt23Si11 (space group F m 3 ¯ m ; a = 1.68052(5) nm). Magnetic susceptibility, electrical resistivity and hea
Publikováno v:
Journal of Alloys and Compounds. 509:6518-6521
Five novel cerium-based ternaries Ce2Rh3.1Si0.9 ,C e 4Rh12Si, Ce8Rh21.9Si3.1, CeRh1.82Si0.18 and CeRh3Si0.125 were studied by means of magnetic susceptibility and electrical resistivity measurements. All these phases were found to be Pauli paramagnet
Publikováno v:
Russian Journal of Inorganic Chemistry. 56:218-222
A study of phase equilibria in the Ce-Ru-In ternary system showed the presence of a new ternary compound Ce16Ru8+xIn3−x, which exists in the range of 0 < x < 1.0. According to a single-crystal X-ray diffraction study of Ce16Ru8+xIn3−x (x = 0.29),
Publikováno v:
Chemistry of Metals and Alloys. 3:101-107