Publikováno v:
Journal of Materials Research and Technology, Vol 21, Iss , Pp 3014-3024 (2022)
The effect of HCO3− and Cl− on the corrosion behavior of Q345 carbon steel in soil simulated solutions was investigated through electrochemical and surface characterizations. The results show that the sample behaves with active dissolution state
Externí odkaz:
https://doaj.org/article/c1328f3a2b1a40f7bcf5607a24a92756
Publikováno v:
Electronic Journal of Differential Equations, Vol 2022, Iss 37,, Pp 1-15 (2022)
Externí odkaz:
https://doaj.org/article/4430250ec3354dc6b4ea365bc8b3f8fe
Publikováno v:
Journal of Magnesium and Alloys, Vol 9, Iss 4, Pp 1220-1232 (2021)
Coatings on the surface of Mg alloys are inevitably damaged during their practical applications, and corrosion can easily initiate from the damaged areas to accelerate the failure of Mg parts. A dual self-healing coating has already been developed to
Externí odkaz:
https://doaj.org/article/0523dd3cb82f4a409bc9a840122b8f5f
Publikováno v:
Corrosion Reviews. 41:5-20
Titanium and its alloys show outstanding application prospects in many industrial fields due to their high specific strength, good corrosion resistance, high temperature resistance, etc. However, at present the corrosion failure of Ti alloys is attra
Publikováno v:
Materials and Corrosion. 74:145-158
Publikováno v:
Journal of Magnesium and Alloys, Vol 5, Iss 1, Pp 26-34 (2017)
The influence of yttrium on the corrosion behavior of Mg–Y alloys has been investigated by electrochemical measurements, scanning electron microscope (SEM) observation, X-ray diffraction (XRD), and X-ray photoelectron spectroscopy (XPS) analysis in
Externí odkaz:
https://doaj.org/article/34fab6e7d8c04412afbd657049dee331
Publikováno v:
Acta Metallurgica Sinica (English Letters). 35:1559-1571
Publikováno v:
Electrochimica Acta. 454:142375
Publikováno v:
Journal of Magnesium and Alloys, Vol 9, Iss 4, Pp 1220-1232 (2021)
Coatings on the surface of Mg alloys are inevitably damaged during their practical applications, and corrosion can easily initiate from the damaged areas to accelerate the failure of Mg parts. A dual self-healing coating has already been developed to