Xuecheng Zhang, Guanghao Guo, Zixin Li, Wenchao Meng, Yuefei Zhang, Qing Ye, Jin Wang, Shibo He, Xinbao Zhao, Jiming Chen, Ze Zhang
Publikováno v:
Communications Engineering, Vol 3, Iss 1, Pp 1-10 (2024)
Abstract Superalloy materials exhibit susceptibility to fracture failures stemming from the influence of thermomechanical factors. To comprehensively understand the fracture mechanisms, material properties, root causes of failure, and the subsequent
Externí odkaz:
https://doaj.org/article/28958469721e4559a4354d3f393f537e
Autor:
Shuli Zeng, Xinbao Zhao, Wanshun Xia, Yunpeng Fan, Lijie Qiao, Yuan Cheng, Hao Liu, Quanzhao Yue, Yuefeng Gu, Ze Zhang
Publikováno v:
Journal of Materials Research and Technology, Vol 30, Iss , Pp 6254-6264 (2024)
This work conducted tensile experiments from room temperature to 1100 °C on a new fourth-generation single crystal superalloys along [001]. The effect of temperature on the tensile properties and deformation mechanism of the alloy were investigated.
Externí odkaz:
https://doaj.org/article/6f4210f384ea42b99dc219d5c8d0fa71
Autor:
Weiqi Li, Xinbao Zhao, Jiachen Xu, Hao Liu, Yuan Cheng, Quanzhao Yue, Wanshun Xia, Yuefeng Gu, Ze Zhang
Publikováno v:
Journal of Materials Research and Technology, Vol 29, Iss , Pp 1453-1466 (2024)
The isothermal oxidation behavior of fourth-generation nickel-based single crystal superalloys with 2-4 wt% Mo content were studied at 900 °C and 1100 °C.At 1100 °C, the oxide layer can be divided into three layers, the outermost layer is Ni–Co
Externí odkaz:
https://doaj.org/article/1050e3118cc74dae980c13c3f7ea691f
Publikováno v:
European Radiology Experimental, Vol 7, Iss 1, Pp 1-9 (2023)
Abstract Background Renal ischemia–reperfusion injury (IRI) frequently occurs clinically. We investigated the value of contrast-enhanced ultrasonography (CEUS) in the evaluation of renal IRI levels in mice. Methods Thirty-six healthy adult male C57
Externí odkaz:
https://doaj.org/article/dc270fe110de4d31918c1a9dbe304651
Publikováno v:
BIO Integration, Vol 4, Iss 3, Pp 84-96 (2023)
Background: Ovarian cancer (OV) is the fifth leading cause of cancer death among women. Growing evidence supports a key role of the tumor microenvironment in the growth, progression, and metastasis of OV. However, the prognostic effects of gene expre
Externí odkaz:
https://doaj.org/article/fdd6c36dfddc4cb39b56ee985918d7a9
Autor:
Yuan Cheng, Xinbao Zhao, Quanzhao Yue, Wanshun Xia, Qinghai Pan, Yu Zhou, Yuefeng Gu, Ze Zhang
Publikováno v:
Materials Research Letters, Vol 11, Iss 11, Pp 957-963 (2023)
Here we investigated the nucleation of the Re, Ru-rich δ phase affected by stacking faults in the γ phase in a 4th generation Ni-based single crystal superalloy during the service at 800°C. The stacking faults in the γ phase were rich in Re and R
Externí odkaz:
https://doaj.org/article/456e9dae913c41648910ee86105ff473
Publikováno v:
Journal of Materials Research and Technology, Vol 24, Iss , Pp 6854-6860 (2023)
The application of commercially pure titanium (CP–Ti) has long been limited by its insufficient strength and plastic instability. However, strength enhancement typically comes at the expense of ductility since the two important mechanical propertie
Externí odkaz:
https://doaj.org/article/16fc7413b62f4abd91825de48e665403
Autor:
Pengfei Wang, Xinbao Zhao, Quanzhao Yue, Wanshun Xia, Qingqing Ding, Hongbin Bei, Yuefeng Gu, Xiao Wei, Ze Zhang
Publikováno v:
Journal of Materials Research and Technology, Vol 24, Iss , Pp 2053-2063 (2023)
Ni-based single-crystal superalloys are extensively employed in turbine blades for aircraft and industrial gas engines. The blades are subjected to complex thermal and stress impacts during service, which may cause sudden low-cycle fatigue damage and
Externí odkaz:
https://doaj.org/article/1639403113b34994813f7f59c99fa963
Publikováno v:
Materials & Design, Vol 237, Iss , Pp 112582- (2024)
The nucleation and growth of topologically close-packed (TCP) phases in Ni-based single crystal superalloys (SCs) are controlled by composition, temperature, time, interface structure and stress. The formation of TCP phases causes detrimental effects
Externí odkaz:
https://doaj.org/article/49765e4011b448fd9c939433de7170ee
Publikováno v:
Metals, Vol 14, Iss 3, p 254 (2024)
Crack initiation plays a major role in very high cycle fatigue (VHCF) life, and the initiation of cracks is related to slip behavior. There is a need for improvement in the understanding of the influence of Ti-6Al-4V microstructures on VHCF performan