Zobrazeno 1 - 10
of 27
pro vyhledávání: '"Xi-tang Wang"'
Publikováno v:
Journal of Iron and Steel Research International. 29:1145-1151
Publikováno v:
Journal of Iron and Steel Research International.
Autor:
Meng Li Qin1, Xi Tang Wang1 wangxt_wust@126.com, Zhou Fu Wang1 whwxt888@163.ne, Yan Ma1, Hao Liu1
Publikováno v:
International Journal of Applied Ceramic Technology. Jul/Aug2018, Vol. 15 Issue 4, p1047-1053. 7p.
Publikováno v:
Solid State Phenomena. 281:111-117
High density MgAl2O4/YAG (yttrium aluminum garnet) eutectic composites were successfully prepared by in-situ reaction sintering using induction heating (IH). The effects of IH time and the starting materials composition on the phase composition and m
Publikováno v:
Solid State Phenomena. 281:255-260
MgAl2O4-Y3Al5O12 ceramic composites were prepared using fused spinel and a Y2O3 micropowder as the raw materials. The microstructure and thermal properties of the composites were characterized by X-ray diffraction, scanning electron microscopy, laser
Publikováno v:
Solid State Phenomena. 281:156-162
The influence of the light burning temperature on the sintering property of nature dolomite has been investigated by two-step sintering process in the temperature range 1500 °C to 1600 °C. The resulting bulk densities and apparent porosities of the
Publikováno v:
Solid State Phenomena. 281:99-104
In order to synthesize cordierite ceramics with low thermal expansion coefficient and good properties, in our work, the cordierite ceramics were prepared by using talc, natural containing zirconium kyanite, common kyanite and industrial Al2O3 as raw
Publikováno v:
International Journal of Applied Ceramic Technology. 14:3-8
Forsterite powders with controllable morphology were synthesized using oxides as raw materials in NaCl–KCl molten salt media. The effects of MgO/SiO2 ratio, calcining temperature, and salt/oxide ratio on the phase composition and morphology of the
Autor:
Yan Ma, Cheng Yan Yang, Zhuo Wang, Wen Wu Zeng, Zhong Tang Zhang, Xi Tang Wang, Zhou Fu Wang, Hao Liu, Qian Zou
Publikováno v:
Journal of Materials Science: Materials in Electronics. 26:8581-8587
YMn0.8Fe0.2O3 ceramics were annealed in oxygen and nitrogen atmosphere, respectively, and the magnetic and dielectric properties were investigated. The structures of the annealed ceramics were maintained in hexagonal P63cm space group. The magnetic s
Publikováno v:
Advanced Materials Research. :1035-1039
Porous silica ceramics were prepared from rice husk ash with a small amount of soft clay as workability agent by the in situ combustion pore-forming technique. Then, the effects of the forming pressures on the linear shrinkage, density, porosity, abs