Dean Heiling, Wayne Reitz
Publikováno v:
Journal of Failure Analysis and Prevention. 17:1019-1022
A radiator hose clamp failed on a motorcycle resulting in loss of traction and a crash. This paper describes the analysis and findings regarding the failure mechanism of the subject hose clamp. Reuse of the hose clamp, rather than replacement during
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::d26828a75e6a71828d29a70bd48615cb
https://doi.org/10.1007/s11668-017-0337-9
https://doi.org/10.1007/s11668-017-0337-9
Autor:
Wayne Reitz
Both rods in a Harrington rod cervical stent failed after a short time in service. Metallurgical analysis revealed a significant number of notches as well as enlarged grain size in one of the two rods, rough shallow-cracked surfaces along the bend pr
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::ba01192a138c89982d41aeed9a1dfe30
https://doi.org/10.31399/asm.fach.v03.c9001801
https://doi.org/10.31399/asm.fach.v03.c9001801
Autor:
Wayne Reitz
Arms bolted to powerline towers were falling off two weeks after installation. Metallurgical and chemical analysis performed on the base metal, weld zone, and heat-affected zone showed acceptable quality material. Residual stress appeared to be respo
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::0559849fa01fff415392b8b67b0d23d3
https://doi.org/10.31399/asm.fach.bldgs.c9001618
https://doi.org/10.31399/asm.fach.bldgs.c9001618
Publikováno v:
Journal of Failure Analysis and Prevention. 16:49-54
A porcelain faucet handle failed after years of use in a residential rental property. Determining the cause of failure was hampered by the fact that the failed handle was no longer available. The analysis included mechanical testing of exemplar fauce
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::e3c3b18c1ade81ee0e0acc5aa6a4f68e
https://doi.org/10.1007/s11668-015-0045-2
https://doi.org/10.1007/s11668-015-0045-2
Autor:
Wayne Reitz
Publikováno v:
Journal of Failure Analysis and Prevention. 13:678-683
Harrington rods failed after a short period in service. Metallurgical analysis showed (1) notches were present on the rods, (2) small cracks present in the bent regions of the rod, and (3) the fractures occurred at clamped locations. All of these con
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::e111704aac76177eb07bf30eb7202ef7
https://doi.org/10.1007/s11668-013-9749-3
https://doi.org/10.1007/s11668-013-9749-3
Autor:
Wayne Reitz
Publikováno v:
Journal of Failure Analysis and Prevention. 13:551-554
An agricultural grain cart rolled over during harvest when a bolt in the hitch assembly failed. The bolt failed due to high shear stress in a thread root. The bolt would not have failed under the same conditions if the threads were not present in the
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::1b39121c3d34a92cf15964d40d7e4a70
https://doi.org/10.1007/s11668-013-9718-x
https://doi.org/10.1007/s11668-013-9718-x
Autor:
Wayne Reitz
Publikováno v:
Journal of Failure Analysis and Prevention. 11:618-623
A 3-million gallon petroleum storage tank was fabricated in the Midwest using A516 steel. The initial fabrication schedule had become compressed; welders worked hurriedly and did not produce good welds. Numerous welds had to be repaired via grinding
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::3ffb977ec79072e46fc9a0588feb7211
https://doi.org/10.1007/s11668-011-9505-5
https://doi.org/10.1007/s11668-011-9505-5
Autor:
Corey J. Isaak, Wayne Reitz
Publikováno v:
Materials and Manufacturing Processes. 23:82-91
The mechanical properties of many materials have been enhanced via cryogenic treatment, which is a cold temperature process performed after traditional heat treatment. In this research the effect of cryogenic treatment on GRCop-84 was examined. Cryog
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::ac5025bf83bd9c3140394f283f6cb591
https://doi.org/10.1080/10426910701524626
https://doi.org/10.1080/10426910701524626
Autor:
Wayne Reitz
Publikováno v:
Practical Failure Analysis. 2:80-84
Arms bolted to powerline towers were falling off two weeks after installation. Metallurgical and chemical analysis performed on the base metal, weld zone, and heat-affected zone (HAZ) showed acceptable-quality material. Residual stress appeared to be
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::292ea3c88d1a87c211f7576f68ac5c01
https://doi.org/10.1007/bf02715503
https://doi.org/10.1007/bf02715503
Autor:
Wayne Reitz
Publikováno v:
Practical Failure Analysis. 2:45-49
Critical heat exchanger components are usually manufactured from durable steels, such as stainless steel, which exhibit good strength and corrosion resistance. Failure of a heat exchanger occurred due to specification of a plain carbon steel that did
Externí odkaz:
https://explore.openaire.eu/search/publication?articleId=doi_________::0df84298e596b2b433de31eb0c366e04
https://doi.org/10.1007/bf02719189
https://doi.org/10.1007/bf02719189