Publikováno v:
Refractories and Industrial Ceramics. 50:131-135
Comprehensive studies have established that ShPDM-45 refractory produced by OAO Zaporozhogneupor exhibits good anticorrosion properties towards the action of electrolysis bath corrosive extraneous components. The degree of degradation of ShPDM-45 ref
Autor:
B. P. Sereda, V. V. Sharapova, D. Yu. Bogoslavskii, V. D. Troyan, I. P. Malyshev, N. A. Troshenkov
Publikováno v:
Refractories and Industrial Ceramics. 49:9-13
Optical microscopy is used to determine wetting angles for aluminosilicate refractories with molten industrial electrolyte and NaF. Kinetic wetting parameters and interaction of electrolyte with refractory are determined. It is shown that removal of
Autor:
D. Yu. Boguslavskii, V. V. Sharapova, V. D. Troyan, B. P. Sereda, I. P. Malyshev, N. A. Troshenkov
Publikováno v:
Refractories and Industrial Ceramics. 48:317-322
Data are provided for laboratory studies of the resistance of aluminosilicate refractories to the action of commercial electrolyte. It is established that refractory ShPDM-45, prepared using a mullite-corundum chamotte, is most resistant to electroly
Autor:
V. D. Troyan, D. Yu. Boguslavskii, I. P. Malyshev, V. V. Sharapova, B. P. Sereda, N. A. Troshenkov
Publikováno v:
Refractories and Industrial Ceramics. 48:246-249
Comparative analysis is provided for the structure and properties of aluminosilicate refractories grade ShPD. It is established that refractory ShPDM-45, produced with the use of an addition of mullite-corundum chamotte surpasses in all characteristi
Autor:
V. N. Pribora, N. M. Odukalets, A. V. Likhodievskii, Yu. V. Lukichev, V. D. Troyan, N. A. Troshenkov, I. P. Malyshev, A. N. Pyrikov
Publikováno v:
Refractories and Industrial Ceramics. 48:12-16
A study has been made of the causes of failure in MLS-62 refractories made by the Zaporozhogneupor Company in order to increase the resistance of the lining in a lime-regenerating rotating oven at the caustic and lime regeneration process for cellulo
Publikováno v:
Refractories and Industrial Ceramics. 41:56-59
Results of introduction of a technology of mullite-corundum refractories with partial replacement of alumina by normal electrocorundum sludge is described. The process of joint milling of alumina and sludge, the firing of chamotte, and the properties
Publikováno v:
Refractories and Industrial Ceramics. 41:345-348
Phase transformations in slime of normal electrocorundum upon heating in air and its high-temperature interaction with kaolin in steady and interspersing layers are studied. Preliminary oxidation of lower titanium oxides contained in slime is a neces
Publikováno v:
Refractories. 37:281-284
Basic parameters of a resource-saving technology for manufacturing unfired articles for bottom steel casting that was developed under laboratory conditions are presented. Industrial tests of an experimental batch of unfired bottom tubes produced by t
Autor:
N. F. Klimkovich, N. G. Aleinikov, N. A. Troshenkov, P. I. Novokhat'ko, L. S. Chmul, Yu. F. Kostyrya, N. F. Grosheva, I. P. Malyshev, O. F. Koshelenko, V. D. Troyan
Publikováno v:
Refractories. 32:154-156
The possibility and desirability of using wastes from the production of silicon carbide articles from the Zaporozhe refractory material factory as a filler mixture for ramming the channels of blast furnaces instead of scarce coke fines which are the
Autor:
B. P. Sereda, V. V. Sharapova, V. D. Troyan, D. Yu. Boguslavskii, I. P. Malyshev, N. A. Troshenkov
Publikováno v:
Refractories and Industrial Ceramics. 48:395-396
The compositions of glasses formed in the process of operation of an aluminum electrolyzer, the lowest content of aluminum at which the glass is separated into aluminosilicate and oxyfluoride components, and the temperatures of softening and of forma