Stress corrosion crack initiation in filler metal 82 in oxygenated high-temperature water

Autor: N. Supornpaibul, J. Duff, M.G. Burke, Y. Wang, F. Scenini

Publikováno v: Supornpaibul, N, Duff, J, Burke, M G, Wang, Y & Scenini, F 2023, ' Stress corrosion crack initiation in filler metal 82 in oxygenated high-temperature water ', Corrosion Science, vol. 214, 111008 . https://doi.org/10.1016/j.corsci.2023.111008

The Stress Corrosion Cracking (SCC) initiation in filler metal (FM) 82 was studied in oxygenated (O2) water at 288 °C. Post-test microstructural characterization revealed that cracked grain boundaries (GBs) always exhibited a porous oxide incursion.