Senkowicz, B. J., Mungall, R. J., Zhu, Y., Jiang, J., Voyles, P. M., Hellstrom, E. E., Larbalestier, D. C.
Magnesium diboride (MgB2) powder was mechanically alloyed by high energy ball milling with C to a composition of Mg(B0.95C0.05)2 and then sintered at 1000 C in a hot isostatic press. Milling times varied from 1 minute to 3000 minutes. Full C incorpor
Externí odkaz:
http://arxiv.org/abs/0712.2056
Autor:
Senkowicz, B. J., Moyet, R. Perez, Mungall, R. J., Hedstrom, J., Uwakweh, O. N. C., Hellstrom, E. E., Larbalestier, D. C.
Magnesium diboride bulk pellets were fabricated from pre-reacted MgB2 powder ball milled with different amounts of exposure to air. Evidence of increased electron scattering including increased resistivity, depressed Tc, and enhanced Hc2 of the mille
Externí odkaz:
http://arxiv.org/abs/cond-mat/0608692
Carbon-doped magnesium diboride was fabricated from pre-reacted pure MgB2 by mechanical alloying. The sample set had excellent critical current densities Jc(8T,4.2K) ranging from 15-60 kA/cm2, depending on composition. Magneto-optical imaging detecte
Externí odkaz:
http://arxiv.org/abs/cond-mat/0603800
Autor:
Senkowicz, B. J., Giencke, J. E., Patnaik, S., Eom, C. B., Hellstrom, E. E., Larbalestier, D. C.
Publikováno v:
Appl. Phys. Lett. 86, 202502 (2005)
High energy milling of MgB2 pre-reacted powder renders the material largely amorphous through extreme mechanical deformation and is suitable for mechanically alloying MgB2 with dopants including carbon. Bulk samples of milled C and MgB2 powders subje
Externí odkaz:
http://arxiv.org/abs/cond-mat/0411199
Autor:
Zhu, Y., Matsumoto, A., Senkowicz, B. J., Kumakura, H., Kitaguchi, H., Jewell, M. C., Hellstrom, E. E., Larbalestier, D. C., Voyles, P. M.
Publikováno v:
Journal of Applied Physics; 7/1/2007, Vol. 102 Issue 1, p013913, 9p, 4 Diagrams, 4 Charts, 6 Graphs
Autor:
Senkowicz, B. J.1 bjsenkowicz@wisc.edu, Takayasu, M.2, Lee, P. J.1, Minervini, J. V.2, Larbalestier, D. C.1
Publikováno v:
IEEE Transactions on Applied Superconductivity. Jun2005 Part 3 of 3, Vol. 15 Issue 2, p3470-3473. 4p.
Publikováno v:
AIP Conference Proceedings; 3/3/2008, Vol. 986 Issue 1, p359-366, 8p, 1 Chart, 7 Graphs
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.