Publikováno v:
MATEC Web of Conferences, Vol 321, p 04025 (2020)
Hot salt stress-corrosion cracking (HSSCC) of titanium alloys has been found in the presence of chloride and other halide salts. Here, a series of AgCl HSSCC tests on Ti-6246 were conducted using a two-point bending rig at 380-500°C to determine the
Externí odkaz:
https://doaj.org/article/2ac16a3c2bb14303b8524674b10dd972
The effect of notch size on fatigue crack threshold and propagation in cast gamma titanium aluminide
Publikováno v:
MATEC Web of Conferences, Vol 321, p 08006 (2020)
Cracks were initiated and grown from notched specimens with notch lengths of 0.03 (FIB), 0.06, 0.1 and 0.5 mm (diamond blade), in cast gamma titanium aluminide at 400 oC. Specimens with longer 0.1 and 0.5 mm notches initiated from the notch and show
Externí odkaz:
https://doaj.org/article/109dbe4a407e4aa39f7cdbb9e126fbca
Publikováno v:
MATEC Web of Conferences, Vol 165, p 13006 (2018)
Gas turbine components are strongly affected by cyclic loading during operation, which makes fatigue development the most significant cause of failure or cracking within them. The nature and growth rate of that fatigue is dependent on the stress expe
Externí odkaz:
https://doaj.org/article/6e28dd26ac1b453d8ece6fad645dcb40
Publikováno v:
In NDT and E International July 2024 145
Autor:
Saunders, Edward J., Dadaev, Tokhir, Brook, Mark N., Wakerell, Sarah, Govindasami, Koveela, Rageevakumar, Reshma, Hussain, Nafisa, Osborne, Andrea, Keating, Diana, Lophatananon, Artitaya, Muir, Kenneth R., Darst, Burcu F., Conti, David V., Haiman, Christopher A., Antoniou, Antonis C., Eeles, Rosalind A., Kote-Jarai, Zsofia
Publikováno v:
In European Urology Oncology April 2024 7(2):248-257
Autor:
Shi, Yitong, Joseph, Sudha, Saunders, Edward A., Sandala, Rebecca S., Walker, Adrian, Lindley, Trevor C., Dye, David
The mechanism of AgCl-induced stress corrosion cracking of Ti-6246 was examined at \SI{500}{\mega\pascal} and \SI{380}{\celsius} for \SI{24}{\hour} exposures. SEM and STEM-EDX examination of a FIB-sectioned blister and crack showed that metallic Ag w
Externí odkaz:
http://arxiv.org/abs/2010.13875
Autor:
Chen, Fei, Madduri, Ravi K., Rodriguez, Alex A., Darst, Burcu F., Chou, Alisha, Sheng, Xin, Wang, Anqi, Shen, Jiayi, Saunders, Edward J., Rhie, Suhn K., Bensen, Jeannette T., Ingles, Sue A., Kittles, Rick A., Strom, Sara S., Rybicki, Benjamin A., Nemesure, Barbara, Isaacs, William B., Stanford, Janet L., Zheng, Wei, Sanderson, Maureen, John, Esther M., Park, Jong Y., Xu, Jianfeng, Wang, Ying, Berndt, Sonja I., Huff, Chad D., Yeboah, Edward D., Tettey, Yao, Lachance, Joseph, Tang, Wei, Rentsch, Christopher T., Cho, Kelly, Mcmahon, Benjamin H., Biritwum, Richard B., Adjei, Andrew A., Tay, Evelyn, Truelove, Ann, Niwa, Shelley, Sellers, Thomas A., Yamoah, Kosj, Murphy, Adam B., Crawford, Dana C., Patel, Alpa V., Bush, William S., Aldrich, Melinda C., Cussenot, Olivier, Petrovics, Gyorgy, Cullen, Jennifer, Neslund-Dudas, Christine M., Stern, Mariana C., Kote-Jarai, Zsofia, Govindasami, Koveela, Cook, Michael B., Chokkalingam, Anand P., Hsing, Ann W., Goodman, Phyllis J., Hoffmann, Thomas J., Drake, Bettina F., Hu, Jennifer J., Keaton, Jacob M., Hellwege, Jacklyn N., Clark, Peter E., Jalloh, Mohamed, Gueye, Serigne M., Niang, Lamine, Ogunbiyi, Olufemi, Idowu, Michael O., Popoola, Olufemi, Adebiyi, Akindele O., Aisuodionoe-Shadrach, Oseremen I., Ajibola, Hafees O., Jamda, Mustapha A., Oluwole, Olabode P., Nwegbu, Maxwell, Adusei, Ben, Mante, Sunny, Darkwa-Abrahams, Afua, Mensah, James E., Diop, Halimatou, Van Den Eeden, Stephen K., Blanchet, Pascal, Fowke, Jay H., Casey, Graham, Hennis, Anselm J., Lubwama, Alexander, Thompson, Ian M., Jr., Leach, Robin, Easton, Douglas F., Preuss, Michael H., Loos, Ruth J., Gundell, Susan M., Wan, Peggy, Mohler, James L., Fontham, Elizabeth T., Smith, Gary J., Taylor, Jack A., Srivastava, Shiv, Eeles, Rosaline A., Carpten, John D., Kibel, Adam S., Multigner, Luc, Parent, Marie-Élise, Menegaux, Florence, Cancel-Tassin, Geraldine, Klein, Eric A., Andrews, Caroline, Rebbeck, Timothy R., Brureau, Laurent, Ambs, Stefan, Edwards, Todd L., Watya, Stephen, Chanock, Stephen J., Witte, John S., Blot, William J., Michael Gaziano, J., Justice, Amy C., Conti, David V., Haiman, Christopher A.
Publikováno v:
In European Urology July 2023 84(1):13-21
Hot salt stress corrosion cracking in Ti 6246 alloy has been investigated to elucidate the chemical mechanisms that occur. Cracking was found to initiate beneath salt particles in the presence of oxidation. The observed transgranular fracture was sus
Externí odkaz:
http://arxiv.org/abs/1802.06045
Autor:
Burns, Daniel, Anokian, Ezequiel, Saunders, Edward J., Bristow, Robert G., Fraser, Michael, Reimand, Jüri, Schlomm, Thorsten, Sauter, Guido, Brors, Benedikt, Korbel, Jan, Weischenfeldt, Joachim, Waszak, Sebastian M., Corcoran, Niall M., Jung, Chol-Hee, Pope, Bernard J., Hovens, Chris M., Cancel-Tassin, Géraldine, Cussenot, Olivier, Loda, Massimo, Sander, Chris, Hayes, Vanessa M., Dalsgaard Sorensen, Karina, Lu, Yong-Jie, Hamdy, Freddie C., Foster, Christopher S., Gnanapragasam, Vincent, Butler, Adam, Lynch, Andy G., Massie, Charlie E., Woodcock, Dan J., Cooper, Colin S., Wedge, David C., Brewer, Daniel S., Kote-Jarai, Zsofia, Eeles, Rosalind A.