Publikováno v:
Nuclear Materials and Energy, Vol 16, Iss , Pp 168-174 (2018)
Yttria (Y2O3) dispersed copper alloys were fabricated by an in-situ process combining Mechanical Alloying (MA) and Hot Isostatic Pressing (HIP). In this process, CuO powder was added into Cu(Y) alloy powders halfway during mechanical alloying (MA). T
Externí odkaz:
https://doaj.org/article/2ddabd1b0f874617a89d943d4a15ed88
Publikováno v:
Nuclear Materials and Energy, Vol 15, Iss , Pp 13-16 (2018)
The correlation between microstructure and mechanical property of ion irradiated 12Cr-6Al ODS ferritic steel was studied. Ion irradiation experiments were performed using 10.5 MeV Fe ions up to the nominal displacement damage of 20 dpa with the damag
Externí odkaz:
https://doaj.org/article/c4dc5b489aa04c04b7ef052e46e7b641
Publikováno v:
Nuclear Materials and Energy, Vol 15, Iss , Pp 17-22 (2018)
Advanced oxide dispersion strengthened copper alloys are promising structural materials for application in divertor system of future fusion reactors due to high irradiation resistance, high thermal conductivity, and good mechanical properties. In thi
Externí odkaz:
https://doaj.org/article/c061aff9ce254a8d97881f8d509e8170
Publikováno v:
Nuclear Materials and Energy, Vol 9, Iss C, Pp 342-345 (2016)
The oxide particle coarsening was evaluated at temperature over 1473K by means of transmission electron microscopy (TEM). After annealing of the 9CrODS extruded bar, the size of oxide particles increases while the number density decreases, indicating
Externí odkaz:
https://doaj.org/article/446687bb75b94146b79ef1795dde72fa
Autor:
R. Kamikawa, S. Ukai, N. Oono, T. Kaito, T. Torimaru, A. Kimura, S. Hayashi, H. Masuda, E. Sato
Publikováno v:
Nuclear Materials and Energy, Vol 9, Iss C, Pp 338-341 (2016)
The high-temperature deformation process of the recrystallized 16CrODS ferritic steel was investigated at 1000°C for the stress loading perpendicular to the elongated grain structure. The strain rate was varied in the range from 1.0×10−2 to 1.0×
Externí odkaz:
https://doaj.org/article/582790b1bd7b4b588091e920fb8448aa
Publikováno v:
Nuclear Materials and Energy, Vol 9, Iss C, Pp 378-382 (2016)
Oxide Dispersion Strengthened (ODS) ferritic/martensitic steels have an excellent high temperature strength primarily due to a dislocation pinning effect of nanometric oxide particles. In the present work, the interaction between oxide particles and
Externí odkaz:
https://doaj.org/article/576e3dea516445fea13927b3590a501d
Publikováno v:
Journal of Nuclear Materials. 583:154508
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.