Eberhard Altstadt, Frank Bergner, Jann-Erik Brandenburg, Paul Chekhonin, Jakub Dykas, Mario Houska, Andreas Ulbricht
Publikováno v:
Frontiers in Nuclear Engineering, Vol 3 (2024)
Neutron irradiation causes embrittlement of reactor pressure vessel (RPV) steels. Post-irradiation annealing is capable of partly or fully restoring the unembrittled condition. While annealing at high temperatures (e.g., 475°C) was successfully appl
Externí odkaz:
https://doaj.org/article/0378eacb0ea049799b61a394522c5f11
Publikováno v:
Nuclear Materials and Energy, Vol 37, Iss , Pp 101511- (2023)
Neutron embrittlement of reactor pressure vessel (RPV) steels potentially limits the safe operational time of nuclear reactors. In tested RPV steel samples microcracks are known to originate from cleaved precipitates, inclusions or grain boundaries,
Externí odkaz:
https://doaj.org/article/8889086869e44b79aa5644cffd508eb1
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Autor:
Stefan Ritter, Hans-Peter Seifert
Publikováno v:
Corrosion and Materials Degradation, Vol 3, Iss 2, Pp 178-191 (2022)
Low-alloy reactor pressure vessel steels have a rather low susceptibility to stress corrosion cracking (SCC) in a boiling water reactor (BWR) environment if the high-temperature water contains no anionic impurities. Recent investigations revealed tha
Externí odkaz:
https://doaj.org/article/25c39e7105204705989e20ffb0c73164
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
Akademický článek
Tento výsledek nelze pro nepřihlášené uživatele zobrazit.
K zobrazení výsledku je třeba se přihlásit.
K zobrazení výsledku je třeba se přihlásit.
The embrittlement of reactor pressure vessel (RPV) steels due to neutron irradiation restricts the operating lifetime of nuclear reactors. The reference temperature 𝑇0, obtained from fracture mechanics testing using the Master Curve concept, is a
Externí odkaz:
https://hzdr.qucosa.de/id/qucosa%3A84379
https://hzdr.qucosa.de/api/qucosa%3A84379/attachment/ATT-0/
https://hzdr.qucosa.de/api/qucosa%3A84379/attachment/ATT-0/
Autor:
Svetlana Fedotova, Evgenia Kuleshova
Publikováno v:
Metals, Vol 13, Iss 9, p 1586 (2023)
This paper presents the results of atom probe tomography studies on radiation-induced phase formation in light-water reactor pressure vessel steels after neutron irradiation under various conditions in comparison with the literature data. The given i
Externí odkaz:
https://doaj.org/article/2cc40731a3a64407a59a01c2465d9886
Publikováno v:
工程科学学报, Vol 42, Iss 3, Pp 340-347 (2020)
The addition of certain amounts of Mn in steel has long been known to retard the growth and coarsening of cementite during tempering, which can increase the tempering resistance of carbon steels. It is now well-established that the retarding effect i
Externí odkaz:
https://doaj.org/article/e362b273c43c4d6891ac9f403f613788
Publikováno v:
Applied Sciences, Vol 12, Iss 22, p 11640 (2022)
A novel nondestructive method called magnetic adaptive testing has been previously applied to detect the neutron-irradiation-generated structural changes in reactor pressure vessel steel material. This method has been found to be a useful tool for th
Externí odkaz:
https://doaj.org/article/9339ee16f49841dd82dd8468741f048e